- Polykemi AB POLYelast TPE Z400 Thermoplastic Elastomer, SEBS-based
Polykemi AB POLYelast TPE Z400 Thermoplastic Elastomer, SEBS-based
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE Z400 Thermoplastic Elastomer, SEBS-based.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.017 - 0.024 cm/cm | 0.017 - 0.024 in/in | With Flow; ISO 2577 |
| 0.017 - 0.024 cm/cm | 0.017 - 0.024 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 8.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 40 @Time 15.0 sec |
40 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 4.00 MPa | <= 580 psi | ISO/R527 |
| Elongation at Break | 775 % | 775 % | ISO/R527 |
| 100% Modulus | 0.00120 GPa | 0.174 ksi | ISO/R527 |
| 300% Modulus | 0.00200 GPa | 0.290 ksi | ISO/R527 |
| Tear Strength | 17.0 kN/m | 97.0 pli | D624 |
| Compression Set | 20 % @Temperature 23.0 °C, Time 259000 sec |
20 % @Temperature 73.4 °F, Time 72.0 hour |
DIN 53517 |
| 32 % @Temperature 70.0 °C, Time 86400 sec |
32 % @Temperature 158 °F, Time 24.0 hour |
DIN 53517 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | Low | % of injection pressure |
| Injection Pressure | Low | |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Network Polymers NPP 25-1002
- SABIC Innovative Plastics Lexan® 4404 PPC+PC
- Overview of materials for High Density Polyethylene (HDPE), Carbon Black Filled
- Momentive Performance Materials Addisilâ„¢ 462 E Healthcare Extrusion Grade Heat Cured Rubber
- A. Schulman POLYBATCH™ AO-25 Antioxidant Masterbatch Based in LDPE
- Cytec Cyply® 1002 Epoxy Fiberglass Composite, Isotropic
- Caplinq LINQSTAT™ VCF-41014B
- Park Electrochemical Nelco® N4000-29 Multifunctional Epoxy
- H.C. Starck Amperit® 415.079 CoNiCrAlY (MCrAlY)
Copyright © lookpolymers.com All Rights Reserved