A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE , Olefinic TPE , Thermoplastic Olefinic Elastomer (TPO)
Manufacturer	A. Schulman, Inc.
Trade Name	POLYTROPE™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DescriptionPolytrope TPP 1008-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics suitable for molding large automotive parts such as fascias and air dams. Information provided by A. Schulman.

Physical Properties	Metric	English	Comments
Specific Gravity	0.890 g/cc	0.890 g/cc	ASTM D792
Linear Mold Shrinkage	0.013 cm/cm	0.013 in/in	±0.1 after 30 min.; ASTM D1238
	0.017 cm/cm	0.017 in/in	± 0.1 at 120°C; ASTM D1238
Melt Index of Compound	9.0 g/10 min	9.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	60	60	ASTM D2240
Tensile Strength, Yield	17.2 MPa	2500 psi	ASTM D638
Elongation at Break	550 %	550 %	ASTM D638
Flexural Modulus	0.552 GPa	80.0 ksi	ASTM D790
Gardner Impact	36.0 J @Temperature -30.0 °C	26.6 ft-lb @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
Brittleness Temperature	-50.0 °C	-58.0 °F