Zotefoams Plastazote® LD18 Low Density Polyethylene Foam

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Zotefoams
Trade Name	Plastazote®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zotefoams Plastazote® LD18 Low Density Polyethylene Foam.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams

Physical Properties	Metric	English	Comments
Density	0.0180 g/cc	0.000650 lb/in³	Nominal skin/skin; BS ISO 7214 1998
	0.0180 - 0.0240 g/cc	0.000650 - 0.000867 lb/in³	sheet density
Cell Length	0.500 - 1.00 mm	0.0197 - 0.0394 in
	0.800 mm	0.0315 in	Typical Diameter

Mechanical Properties	Metric	English	Comments
Hardness, Shore OO	50	50	10 mm cell/cell thickness; ISO 868 1985
Tensile Strength	0.300 MPa	43.5 psi	ISO 7214 1998
Elongation at Break	125 %	125 %
Compressive Yield Strength	0.0330 MPa @Strain 10.0 %	4.79 psi @Strain 10.0 %	BS ISO 7214 1998
	0.0500 MPa @Strain 25.0 %	7.25 psi @Strain 25.0 %	BS ISO 7214 1998
	0.0810 MPa @Strain 40.0 %	11.7 psi @Strain 40.0 %	BS ISO 7214 1998
	0.113 MPa @Strain 50.0 %	16.4 psi @Strain 50.0 %	BS ISO 7214 1998
Tear Strength	0.520 kN/m	2.97 pli	BS EN ISO 8067 1995
Compression Set	5.5 % @Time 79200 sec, Strain 25.0 %	5.5 % @Time 22.0 hour, Strain 25.0 %	24 hr recovery; BS ISO 7214 1998
	13 % @Time 79200 sec, Strain 25.0 %	13 % @Time 22.0 hour, Strain 25.0 %	0.5 hr recovery; BS ISO 7214 1998
	18.5 % @Time 79200 sec, Strain 50.0 %	18.5 % @Time 22.0 hour, Strain 50.0 %	24 hr recovery; BS ISO 7214 1998
	27.5 % @Time 79200 sec, Strain 50.0 %	27.5 % @Time 22.0 hour, Strain 50.0 %	0.5 hr recovery; BS ISO 7214 1998

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0446 W/m-K	0.310 BTU-in/hr-ft²-°F	mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air	100 °C	212 °F
Minimum Service Temperature, Air	-70.0 °C	-94.0 °F
Flammability Test	1.7 @Thickness 13.0 mm	1.7 @Thickness 0.512 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998
	2.2 @Thickness 5.00 mm	2.2 @Thickness 0.197 in	Horizontal Burn Rate, mm/sec; ISO 7214 1998