Schmolz + Bickenbach 416 Stainless Steel Bar

Category Metal , Ferrous Metal , Martensitic , Stainless Steel , T 400 Series Stainless Steel
Manufacturer Schmolz + Bickenbach (Swiss Steel International)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Schmolz + Bickenbach 416 Stainless Steel Bar.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Ugitech’s 416 is free machining martensitic grade. The unique production process—developed exclusively by Ugitech—results in a product that delivers superior productivity, tool life and consistency, and improves the surface finish on all types of machined parts. Machined parts are frequently used in the annealed condition, but may be heat treated to develop optimum mechanical properties for specific applications. 416 HT, condition T (HRc26-32), is the popular heat-treated version of 416. This condition is specified for numerous engineering applications, and represents the optimum condition for both machinability and corrosion resistance. No further heat treatment of machined parts is required.Hardened and tempered: Heat and hold 50°F to 100°F (10°C to 40°C) below tempering temperature for 4-7 hours, slow cool.Information provided by Schmolz + Bickenbach
Physical Properties Metric English Comments
Density 7.64 g/cc
0.276 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 264 - 294
264 - 294
Heat Treatment (Condition T HRc 26-32)
190 - 210

@Thickness >=25.4 mm
 190 - 210

@Thickness >=1.00 in
 Turned Bars
190 - 240

@Thickness <=25.4 mm
 190 - 240

@Thickness <=1.00 in
 Cold Drawn Bars
Tensile Strength 889 - 1030 MPa
129000 - 150000 psi
Heat Treatment (Condition T HRc 26-32)
621 - 758 MPa

@Thickness >=25.4 mm
 90000 - 110000 psi

@Thickness >=1.00 in
 Turned Bars
621 - 827 MPa

@Thickness <=25.4 mm
 90000 - 120000 psi

@Thickness <=1.00 in
 Cold Drawn Bars
Tensile Strength, Yield 758 - 896 MPa

@Strain 0.200 %
 110000 - 130000 psi

@Strain 0.200 %
 Heat Treatment (Condition T HRc 26-32)
448 - 586 MPa

@Strain 0.200 %,
Thickness >=25.4 mm
 65000 - 85000 psi

@Strain 0.200 %,
Thickness >=1.00 in
 Turned Bars
552 - 724 MPa

@Strain 0.200 %,
Thickness <=25.4 mm
 80000 - 105000 psi

@Strain 0.200 %,
Thickness <=1.00 in
 Cold Drawn Bars
Elongation at Yield >= 40 %
>= 40 %
Heat Treatment (Condition T HRc 26-32)
>= 10 %

@Thickness <=25.4 mm
 >= 10 %

@Thickness <=1.00 in
 Cold Drawn Bars
>= 20 %

@Thickness >=25.4 mm
 >= 20 %

@Thickness >=1.00 in
 Turned Bars
Reduction of Area >= 5.0 %
>= 5.0 %
Heat Treatment (Condition T HRc 26-32)
>= 40 %

@Thickness <=25.4 mm
 >= 40 %

@Thickness <=1.00 in
 Cold Drawn Bars
>= 60 %

@Thickness >=25.4 mm
 >= 60 %

@Thickness >=1.00 in
 Turned Bars
Modulus of Elasticity 205 GPa
29700 ksi
Tension
Thermal Properties Metric English Comments
CTE, linear 10.8 µm/m-°C

@Temperature 20.0 - 200 °C
 6.00 µin/in-°F

@Temperature 68.0 - 392 °F
Thermal Conductivity 24.9 W/m-K

@Temperature 20.0 °C
 173 BTU-in/hr-ft²-°F

@Temperature 68.0 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.15 %
<= 0.15 %
Chromium, Cr 12 - 14 %
12 - 14 %
Copper, Cu <= 0.50 %
<= 0.50 %
Iron, Fe >= 81.84 %
>= 81.84 %
Manganese, Mn <= 1.25 %
<= 1.25 %
Molybdenum, Mo <= 0.60 %
<= 0.60 %
Phosphorous, P <= 0.060 %
<= 0.060 %
Silicon, Si <= 1.0 %
<= 1.0 %
Sulfur, S >= 0.15 %
>= 0.15 %
Zirconium, Zr <= 0.60 %
<= 0.60 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000559 ohm-cm
0.0000559 ohm-cm
Processing Properties Metric English Comments
Annealing Temperature 649 - 760 °C
1200 - 1400 °F
Sub-critical anneal
899 °C
1650 °F
Softest Properties
<= 593 °C

@Time 14400 - 25200 sec
 <= 1100 °F

@Time 4.00 - 7.00 hour
 Hold for time, slow cool
Hot-Working Temperature 801.7 °C
1475 °F
Slow heating
954 - 1180 °C
1750 - 2150 °F
Forging range
1150 - 1180 °C
2100 - 2150 °F
Then more rapidly
Descriptive Properties Value Comments
Corrosion Resistance Humidity
2/4
Sodium Carbonate
2/4