United Cast Bar Unibar 600-3 Continuously Cast Spheroidal Graphite Iron

Category	Metal , Ferrous Metal , Cast Iron , Gray Cast Iron
Manufacturer	United Cast Bar
Trade Name	Unibar
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	United Cast Bar Unibar 600-3 Continuously Cast Spheroidal Graphite Iron.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Offers reasonable machinability and excellent surface finish combined with higher wear resistance, strength & heat treatment. Noise and vibration damping are good in this grade.Unibar 600-3 can be hardened by conventional methods, to Rc 50 on the bar surface, responds well to austempering (ADI).Information provided by United Cast Bar Ltd.

Physical Properties	Metric	English	Comments
Density	7.30 g/cc	0.264 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Brinell	200 - 270 @Load 3000 kg	200 - 270 @Load 6610 lb	10 mm ball
Tensile Strength	550 MPa @Diameter 105 - 200 mm	79800 psi @Diameter 4.13 - 7.87 in
	550 MPa @Diameter 205 - 600 mm	79800 psi @Diameter 8.07 - 23.6 in
	600 MPa @Diameter 25.0 - 50.0 mm	87000 psi @Diameter 0.984 - 1.97 in
	600 MPa @Diameter 55.0 - 100 mm	87000 psi @Diameter 2.17 - 3.94 in
Tensile Stress	340 MPa @Diameter 105 - 200 mm, Strain 0.200 %	49300 psi @Diameter 4.13 - 7.87 in, Strain 0.200 %
	340 MPa @Diameter 205 - 600 mm, Strain 0.200 %	49300 psi @Diameter 8.07 - 23.6 in, Strain 0.200 %
	360 MPa @Diameter 55.0 - 100 mm, Strain 0.200 %	52200 psi @Diameter 2.17 - 3.94 in, Strain 0.200 %
	370 MPa @Diameter 25.0 - 50.0 mm, Strain 0.200 %	53700 psi @Diameter 0.984 - 1.97 in, Strain 0.200 %
Elongation at Break	1.0 % @Thickness 105 - 200 mm	1.0 % @Thickness 4.13 - 7.87 in
	1.0 % @Thickness 205 - 600 mm	1.0 % @Thickness 8.07 - 23.6 in
	2.0 % @Thickness 55.0 - 100 mm	2.0 % @Thickness 2.17 - 3.94 in
	3.0 % @Thickness 25.0 - 50.0 mm	3.0 % @Thickness 0.984 - 1.97 in

Component Elements Properties	Metric	English	Comments
Carbon, C	3.25 - 3.7 %	3.25 - 3.7 %
Iron, Fe	92.83 - 94.19 %	92.83 - 94.19 %	as balance
Magnesium, Mg	0.040 - 0.070 %	0.040 - 0.070 %
Manganese, Mn	0.10 - 0.30 %	0.10 - 0.30 %
Phosphorous, P	0.015 - 0.080 %	0.015 - 0.080 %
Silicon, Si	2.4 - 3.0 %	2.4 - 3.0 %
Sulfur, S	0.0050 - 0.020 %	0.0050 - 0.020 %