- Solvay TECHNYL® AR 218 V25 Nylon 66, 25% glass fiber, DRY
Solvay TECHNYL® AR 218 V25 Nylon 66, 25% glass fiber, DRY
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® AR 218 V25 Nylon 66, 25% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA66 reinforced with 25% of glass fiber, heat stabilized, containing recycled material.Available in: Europe and North AmericaProduct Applications: TECHNYL® AR 218 V25 BLACK even if it shows slightly lower and more variable mechanical performances than the virgin prime grade TECHNYL® A 218 V25,can be used in all sectors of industry in less demanding applications and fits the main quality standards of Automotive market. This product is available in blackInformation provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 Type 1A |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 Type 1A |
| Tensile Modulus | 7.80 GPa | 1130 ksi | ISO 527 Type 1A |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | ISO 178 |
| Izod Impact, Unnotched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/1U |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C | |
| Mixing Zone | 280-290°C |
Users viewing this material also viewed the following:
- RheTech Products HP514-393 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 110D Medium Dark Pewter
- Quadrant EPP Techtron® PPS unfilled, extruded (ISO Data)
- LyondellBasell Hifaxâ„¢ Thermoplastic Polyolefin Elastomer
- SABIC Innovative Plastics LNP Thermocomp DX99721 PC (Asia Pacific)
- Chicago Extruded Metals UNS C33500 Copper-Zinc-Lead Alloy
- Eurotec® Tecodur® PB70 GR30 NL MB04 PBT/ASA, 30% glass fiber reinforced, heat & UV stabilized, natural
- 3M 8777 Sealing Tape
- Johnson Matthey JM6040 Soft Solder/Flux
- Karina E 02/242-RG-PO Yellow Color Concentrate for PVC
Copyright © lookpolymers.com All Rights Reserved