Solvay Specialty Polymers Ixef® 1032 Polyarylamide (PARA), 60% Glass Fiber (Conditioned)

Category Polymer , Thermoplastic , PVDC , Polyvinyl Dichloride (PVDC)
Manufacturer Solvay Specialty Polymers
Trade Name Ixef®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 1032 Polyarylamide (PARA), 60% Glass Fiber (Conditioned).pdf
  Online Service   lookpolymers   27660005
Material Notes:
Ixef® 1032 is a 60% glass-fiber reinforced, general purpose polyarylamide compound which exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; High Flow; High Strength; Low Moisture Absorption; Outstanding Surface Finish; Ultra High StiffnessUses: Automotive Applications; Automotive Electronics; Automotive Interior Parts; Furniture; High Gloss Applications; Metal Replacement; Sporting GoodsInjection Molding Notes: Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding.Automotive Specifications ASTM D6779 PA111G60; BMW GS 93016; GM GM7001M; GM GM7001M PAMXD6 A4 A22 A64 BA661 DC1770 G30 KS2400 MS1800 NS340 RT7 SS225 Color: 0008 Natural; GM GM7001M PAMXD6 A4 A22 A64 BA661 DC1770 G30 KS2400 MS1800 NS340 RT7 SS225 Color: 9008 BlackInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.77 g/cc
0.0639 lb/in³
Dry; ISO 1183
Filler Content 60 %
60 %
Glass Fiber
Mechanical Properties Metric English Comments
Tensile Strength at Break 250 MPa
36300 psi
ISO 527-2
Elongation at Break 2.0 %
2.0 %
ISO 527-2
Tensile Modulus 23.0 GPa
3340 ksi
ISO 527-2
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Middle Barrel Temperature 260 - 270 °C
500 - 518 °F
Front Barrel Temperature 270 - 280 °C
518 - 536 °F
Nozzle Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 80.0 °C

@Time 43200 sec
176 °F

@Time 12.0 hour
Moisture Content <= 0.30 %
<= 0.30 %
Injection Pressure 50.0 - 150 MPa
7250 - 21800 psi
Hold Pressure 75.0 MPa
10900 psi
Back Pressure 0.000 - 1.00 MPa
0.000 - 145 psi
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Latin America
North America
Color Black; Colors; Natural
Form Pellets
Injection Rate Fast
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant
Screw L/D Ratio 15.0:1.0 to 20.0:1.0