- Acrylonitrile Butadiene Styrene (ABS), Molded
- Samsung Cheil Industries Starex® EA-0640 ABS, Unreinforced
Samsung Cheil Industries Starex® EA-0640 ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® EA-0640 ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Permanent static prevention ABS material such as LCD carrierInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 1.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D785 |
| Tensile Strength at Break | 33.3 MPa | 4830 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 20 % | 20 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.96 GPa | 284 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 73.5 MPa | 10700 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.86 J/cm @Thickness 3.17 mm |
3.49 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 1.96 J/cm @Thickness 6.35 mm |
3.67 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 6.40 mm |
181 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 98.0 °C | 208 °F | B/50; ISO R306 |
| 100 °C | 212 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 6.00 mm |
HB @Thickness 0.0591 - 0.236 in |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S70S Conductive Silicone Rubber
- Lucite International Diakon® ST35G8 Toughened Acrylic Polymer
- SABIC Innovative Plastics Valox® IQ8280SF PBT+PET
- Sichuan Deyang Haton® hc Polyphenylene Sulfide Resin
- Solvay LUBRHOPHOS® LB 400 Surfactant
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 70 PHR N774 (SRF) Filler
- Fainplast Compounds CL 76 Flexible PVC, Sheathing
- Braskem JV060U Injection Molding High Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved