S&E Specialty Polymers GPP1001HFNH-2-AT(18) PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | S&E Specialty Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | S&E Specialty Polymers GPP1001HFNH-2-AT(18) PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: Non-halogen flame retardant UL-94 V0 polypropylene compound.Information provided by S&E Specialty Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 9.0 - 14 g/10 min | 9.0 - 14 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 18.6 MPa | >= 2700 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Modulus | >= 2.17 GPa | >= 315 ksi | ASTM D790 |
| Izod Impact, Notched | >= 0.320 J/cm | >= 0.600 ft-lb/in | ASTM D256 |
| Gardner Impact | >= 16.3 J | >= 12.0 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability Test | 5.0 @Thickness 1.59 mm |
5.0 @Thickness 0.0625 in |
|
| Oxygen Index | >= 34 % | >= 34 % | ASTM D2863 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | >90 L | Colorimeter |
Users viewing this material also viewed the following:
- MV Labs DY800 Dy2O3 Dysprosium oxide
- DSM Biomedical PurSil® AL 20 Aliphatic Thermoplastic Silicone Polyether Urethane (discontinued **)
- Chevron Phillips 4518 LDPE Extrusion Coating Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8534 PEEK, with mineral filler
- Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C
- Solvay Specialty Polymers FOMBLIN® W150 PFPE Lubricant
- Wellman Wellamid® MRT1487 BK Nylon 66, 32% Mineral Reinforced
- BASF Ultramid® B3GK24 10/20% Glass Bead/Fiber Filled PA6 (Dry)
- Braskem HB0454HR HDPE Blow Molding Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved