SABIC Innovative Plastics Valox® 305 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 305 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, For compounding only. Not intended for Injection Molding. Melt viscosity: 250C at 21.6 kgf is 1450-1850.
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Viscosity 100000 cP
100000 cP
Melt Viscosity; SABIC Method
Linear Mold Shrinkage, Flow 0.019 - 0.021 cm/cm

@Thickness 3.20 mm
 0.019 - 0.021 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.020 - 0.022 cm/cm

@Thickness 3.20 mm
 0.020 - 0.022 in/in

@Thickness 0.126 in
 SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 29.0 MPa
4210 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 40.6 %
40.6 %
Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.37 GPa
344 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 148 °C

@Thickness 3.20 mm
 298 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 51.0 °C

@Thickness 3.20 mm
 124 °F

@Thickness 0.126 in
 unannealed; ASTM D648