SABIC Innovative Plastics Lexan® LUX9130T PC COPOLYMER (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® LUX9130T PC COPOLYMER (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LUX9130T Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm / 5VA rating at 6.0mm and is UV stabilized providing additional weathering capability. LUX9130T is high transparency, extremly low haze and bubble free for thick part molding.LUX9130T is available in clear transparent and tinted color options that is an excellent candidate for a wide variety of applications.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.0100 %
0.0100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.10 %
0.10 %
ISO 62
Linear Mold Shrinkage, Flow 0.0045 - 0.0065 cm/cm

@Thickness 3.20 mm
0.0045 - 0.0065 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 18 g/10 min

@Load 1.20 kg,
Temperature 300 °C
18 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 17 g/10 min

@Load 1.20 kg,
Temperature 300 °C
17 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 64.0 MPa
9280 psi
Type I, 50 mm/min; ASTM D638
64.0 MPa
9280 psi
50 mm/min; ISO 527
Elongation at Break 52 %
52 %
50 mm/min; ISO 527
72 %
72 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.37 GPa
344 ksi
50 mm/min; ASTM D638
2.40 GPa
348 ksi
1 mm/min; ISO 527
Flexural Yield Strength 98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.41 GPa
350 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.00 J/cm
1.87 ft-lb/in
ASTM D256
0.900 J/cm

@Temperature -30.0 °C
1.69 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*3; ISO 180/1A
9.00 kJ/m²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) 130 kJ/m²
61.9 ft-lb/in²
80*10*3; ISO 180/1U
130 kJ/m²

@Temperature -30.0 °C
61.9 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 55.0 J

@Temperature 23.0 °C
40.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
74.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
41.1 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 71.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 131 °C
268 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
131 °C

@Thickness 3.20 mm
268 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
120 °C

@Thickness 3.20 mm
248 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 137 °C
279 °F
Rate B/50; ASTM D1525
137 °C
279 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/120; ISO 306
UL RTI, Electrical 115 °C
239 °F
UL 746B
UL RTI, Mechanical with Impact 115 °C
239 °F
UL 746B
Flammability, UL94 V-2

@Thickness 0.400 mm
V-2

@Thickness 0.0157 in
UL 94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VA

@Thickness 6.00 mm
5VA

@Thickness 0.236 in
UL 94
Glow Wire Test 850 °C
1560 °F
IEC 60695-2-13
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
IEC 60695-2-12
Optical Properties Metric English Comments
Transmission, Visible >= 88 %
>= 88 %
6.0 mm; ASTM D1003
>= 89.5 %
>= 89.5 %
3.0 mm; SABIC Method
>= 90 %
>= 90 %
2.0 mm; SABIC Method
>= 90.5 %
>= 90.5 %
1.0 mm; SABIC Method
Electrical Properties Metric English Comments
Dielectric Constant 2.81

@Frequency 1.00e+9 Hz
2.81

@Frequency 1.00e+9 Hz
ASTM ES 7-83
Dissipation Factor 0.0058

@Frequency 1.10e+9 Hz
0.0058

@Frequency 1.10e+9 Hz
ASTM ES 7-83
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Pass
IEC 60695-10-2