SABIC Innovative Plastics LNP Thermocomp MH0200A PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp MH0200A PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* MH0200A is a compound based on Polypropylene resin containing High Specific Gravity Filler.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.91 g/cc | 0.0690 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | on tensile bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 18.0 MPa | 2610 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 25 % | 25 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 33.0 MPa | 4790 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |