Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 18.0 MPa | 2610 psi | |
Plastcom SLOVALEN EH 96 FRD 2 PP, flame retardant FeaturesDetermined for environment, where contact with water is possible, because the electric properties do not change by conditioning. Application - terminals, coil forms, guides in washing machin.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | |
Plastcom SLOVALEN PQ 83 N PP, imp. strength FeaturesPP modified with natural caoutchouc. The addition of thermoplastic caoutchouc causes increased toughness. General application in all industry branches. Delivered in natural mode and in the f.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | |
Plastcom SLOVALEN PC 93 T 5 PP reinforced with 5% mineral filler Features: Modified PP for injection moulding with the content of 5% mineral filling. Increased rigidity, strength and thermal. Decreased shrinkage. General application in all industry branches.Packa.. |
|||
Tensile Strength at Break | <= 18.0 MPa | <= 2610 psi | ISO/R527 |
Polykemi AB POLYfill PPC BGK601213 CR Polypropylene Copolymer, Multifiller Information provided by Polykemi AB |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCA871A PPE (Europe-Africa-Middle East) Flame retardant performance and mechanical properties capable of meeting UL VW-1 requirement and 105C temperature rating as defined UL1581. UL1581 tests conducted on 1.0mmD wire with AWG28 conductor.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCD861A PPE-TPE (Europe-Africa-Middle East) Flexible, migration-improved, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCD891B PPE-TPE (Europe-Africa-Middle East) Non-halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications. Strong flame retardant performance capable of meeting VW-1 and 80°C end use tempera.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 55T1030 PP SABIC® PPcompound 55T1030 is a general purpose, talc filled, heat stabilized copolymer polypropylene compound. This compound exhibits very high impact, and is suitable for multiple processing met.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON TX06488NTX1 PU LNP* STAT-KON* TX06488NTX1 is a compound based on Polyurethane resin containing Proprietary Filler(s). Added features of this grade are: Execllent Ductility, Electrically Conductive. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCD841U PPE-TPE Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame r.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
SCG Chemicals EL-Proâ„¢ P841J Polypropylene Injection Molding Key Characteristics:Excellent flowabilityExcellent processabilityHigh stiffnessSuitable for complex parts and large partsContains UV stabilizer and anti-static agentRecommended Applications:Electric.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO 527 |
A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene DescriptionPolyfort® FPP 1182E is a 20% talc-filled, extrusion grade copolymer polypropylene. It had a good balance of flexural modulus, low temperature impact, and appearance properties. Informat.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
UBE F019 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D 638 |
Cossa Polimeri ESTAPROP 1050 V0 HF K Flame Retardant Polypropylene PP copolymerFlame retardant class V0, halogen free, excellent mechanical characteristics, excellent processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ CMU 101D Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive interior trim in which good surface finish, high scratch resistance, minimum dust deposit and good UV resistan.. |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ISO R 527 |
Fainplast Compounds CL 81 Flexible PVC, Sheathing General purposes |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | ISO R 527 |
Fainplast Compounds GA 75/R Flexible PVC, Flame Retardant Sheathing According to UL 1581 Class 43 (90°C) |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO R 527 |
Fainplast Compounds MPH 78/OP Medical Flexible PVC, Extrusion Tubolar apparatus anti bend |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO R 527 |
Fainplast Compounds MPH 83/T Medical Flexible PVC, Extrusion Technical tubes no DOP |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436C10L Calcium Reinforced |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436C10L1 Calcium Reinforced |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
Arkema Group OREVAC® 9309 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 |
Aclo Accuguard Polypropylene CP0467V2CSL Copolymer Flame Retardant Copper Stabilized |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO R 527 |
Fainplast Compounds MPH 85 Medical Flexible PVC, Extrusion Tubolar apparatus |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO R 527 |
Fainplast Compounds PM 8012 Flexible PVC, Lead Free Various profiles |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics SABIC PPCOMPOUND 15T1020 PP SABIC® PPcompound 15T1020. This grade is a general purpose, talc filled, heat stabilized polypropylene resin suitable for injection molded applications. The IMDS ID is 16486973. |
|||
Tensile Strength at Break | >= 18.0 MPa | >= 2610 psi | |
Shandong Dongyue Shenzhou New Material Co DS608 Fluorinated Ethylene-Propylene Copolymer For High-Speed Extrusion Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene is the copolymer of TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, and low coeff.. |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO R 527 |
Fainplast Compounds GS 8004 Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO R 527 |
Fainplast Compounds PM 8020 Flexible PVC, Lead Free Covering steel sheaths |