SABIC Innovative Plastics LNP Thermocomp EC002E PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp EC002E PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* EC002E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ASTM D 792
1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.35 %
0.35 %
23°C / 50% RH; ISO 62
0.30 %

@Time 86400 sec
0.30 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D 955
0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D 955
0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 137 MPa
19900 psi
ISO 527
161 MPa
23400 psi
ASTM D 638
Elongation at Break 1.2 %
1.2 %
ISO 527
1.6 %
1.6 %
ASTM D 638
Tensile Modulus 11.65 GPa
1690 ksi
50 mm/min; ASTM D 638
12.63 GPa
1832 ksi
1 mm/min; ISO 527
Flexural Strength 216 MPa
31300 psi
ISO 178
241 MPa
35000 psi
ASTM D 790
Flexural Modulus 10.31 GPa
1495 ksi
ISO 178
10.8 GPa
1570 ksi
ASTM D 790
Izod Impact, Notched 0.530 J/cm

@Temperature 23.0 °C
0.993 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 4.27 J/cm

@Temperature 23.0 °C
8.00 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 28.0 kJ/m²

@Temperature 23.0 °C
13.3 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
11.0 J

@Temperature 23.0 °C
8.11 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 33.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
18.5 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
34.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
19.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 32.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
18.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
33.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
18.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
205 °C

@Thickness 3.20 mm
401 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D 257