SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* ZF006 is a compound based on PPE+PS resin containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0900 % | 0.0900 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | 5 mm/min; ISO 527 |
| 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| 1.8 % | 1.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 8.76 GPa | 1270 ksi | 1 mm/min; ISO 527 |
| 9.21 GPa | 1340 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 156 MPa | 22600 psi | ISO 178 |
| 161 MPa | 23400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 8.31 GPa | 1210 ksi | 2 mm/min; ISO 178 |
| 8.63 GPa | 1250 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.09 J/cm | 2.04 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.54 J/cm | 8.51 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 30.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® SOL T 6302 Styrene - Butadiene Block Copolymer
- SABIC Innovative Plastics Lexan® EXL4016 PC Copolymer (Asia Pacific)
- Glastic Laminates/Shapes 1603-2D Fiberglass-Reinforced Polyester Standoff Insulator
- Techmer ES HiFill® PP 0254 S Polypropylene
- Samsung Cheil Industries Starex® MG-0330 ABS, Unreinforced Heat Resistant
- Techmer ES HiFill® PA6/6 LGF60 HS L BK 12 mm
- DuPont™ Fusabond® A560 Polymer Modifier
- DuPont Performance Polymers Delrin® 100AL NC010 Acetal (POM) (Unverified Data**)
- CMW® D581F Silver Graphite Contact Material
- Ascend Performance Materials Vydyne® 21FSR Nylon 66, General Purpose