Polymer Property : Tensile Strength at Break = 111 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HFD4413 PC
Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HFD4413 PC (Asia Pacific)
Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Tensile Strength at Break 111 MPa
16100 psi
5 mm/min; ISO 527
Lavergne VYPET VNT 340 PET 40% Glass - Mineral Reinforced
Vypet VNT 340 is a 40% glass/mineral reinforced PET injection molding compound designed for electrical and structural applications, with High Dielectric StrengthFeatures: High temperature performanc..
Tensile Strength at Break 111 MPa
16100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DE0026 PC (Europe-Africa-Middle East)
LNP* Stat-kon* DC-1002 FR is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Flame Retardant, Electrically Conductive.
Tensile Strength at Break 111 MPa
16100 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON DX04489C PC
LNP STAT-KON* DX04489C is a high modulus compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Con..
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Valox® SHF436HR PBT
PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant.
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Valox® SHF436HR PBT (Asia Pacific)
PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant.
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Valox® SHF436HR PBT (Europe-Africa-Middle East)
PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant.
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC
LNP* Stat-kon* Lexan_LC1500N compound is a 15% carbon fiber, 6% PTFE reinforced polycarbonate.
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Europe-Africa-Middle East)
LNP* Stat-kon* Lexan_LCF1506 is a 15% carbon fiber, 6% PTFE reinforced polycarbonate.
Tensile Strength at Break 111 MPa
16100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Stat-kon ZX05043 PPE+PS (Europe-Africa-Middle East)
LNP* Stat-kon* ZX05043 is a compound based on PPE+PS Blend resin containing Glass Fiber, PTFE, Carbon Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break 111 MPa
16100 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX06410 PC (Asia Pacific)
LNP* Thermocomp* DX06410 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Tensile Strength at Break 111 MPa
16100 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QF004 PA 6/10
LNP* THERMOCOMP* QF004 is a compound based on Nylon 6/10 resin containing 20% Glass Fiber.
Tensile Strength at Break 111 MPa
16100 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QF004 PA 6/10 (Asia Pacific)
LNP* Thermocomp* QF004 is a compound based on Nylon 6/10 resin containing Glass Fiber.
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP WF006L PBT
LNP* THERMOCOMP* WF006L is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this material is: Low Extractible.
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS
LNP* THERMOCOMP* ZF006 is a compound based on PPE+PS resin containing 30% Glass Fiber.
Tensile Strength at Break 111 MPa
16100 psi
ASTM D638
SABIC Innovative Plastics LNP STAT-KON DEL36 PC (Asia Pacific)
LNP* Stat-kon* DEL36 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, , Internally Lubricated.
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp LFZ42XXC PEEK
LNP THERMOCOMP* LFZ42XXC is a compound based on Polyetheretherketone resin containing Glass Fiber, Milled Glass. Added features of this material include: Low Warpage.This data was supplied by SABIC..
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HFD4413 PC (Europe-Africa-Middle East)
Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Tensile Strength at Break 111 MPa
16100 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Asia Pacific)
15% carbon fiber, 6% PTFE reinforced polycarbonate.
Tensile Strength at Break 111 MPa
16100 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX06410 PC
LNP* THERMOCOMP* DX06410 is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.