SABIC Innovative Plastics LNP THERMOCOMP RC006H PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RC006H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RC006H is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| 1.278 g/cc | 0.04617 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.650 % | 0.650 % | 50% RH, 24 hrs; ASTM D570 |
| 1.14 % | 1.14 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00080 cm/cm @Time 86400 sec |
0.00080 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0056 cm/cm @Time 86400 sec |
0.0056 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 266 MPa | 38600 psi | Type I, 5 mm/min; ASTM D638 |
| 271 MPa | 39300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 |
| 1.9 % | 1.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 22.65 GPa | 3285 ksi | 1 mm/min; ISO 527 |
| 27.78 GPa | 4029 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 408 MPa | 59200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 18.75 GPa | 2719 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 21.02 GPa | 3049 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.14 J/cm | 19.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 68.0 kJ/m² | 32.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J | 10.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.36 | 0.36 | ASTM D3702 Modified |
| K (wear) Factor | 40.3 x 10-8 mm³/N-M | 20.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
6.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 11.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
6.39 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 |