SABIC Innovative Plastics LNP THERMOCOMP QF00A PA 6/10 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP QF00A PA 6/10 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* QF00A is a compound based on Nylon 6/10 resin containing Glass Fiber.
Physical Properties Metric English Comments
Density 1.51 g/cc
0.0546 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
on Tensile Bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 180 MPa
26100 psi
5 mm/min; ISO 527
Elongation at Break 3.7 %
3.7 %
5 mm/min; ISO 527
Tensile Modulus 10.9 GPa
1580 ksi
1 mm/min; ISO 527
Flexural Yield Strength 265 MPa
38400 psi
2 mm/min; ISO 178
Flexural Modulus 10.6 GPa
1540 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 19.0 kJ/m²
9.04 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 95.0 kJ/m²
45.2 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 17.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 9.44 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 93.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 51.7 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 201 °C
394 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af