SABIC Innovative Plastics LNP STAT-KON EEF42 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON EEF42 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* EEF42 is a compound based on Polyetherimide resin containing Carbon Fiber, Glass Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Time 86400 sec |
0.0010 - 0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0040 cm/cm @Time 86400 sec |
0.0030 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 194 MPa | 28100 psi | ASTM D638 |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| Tensile Modulus | 15.85 GPa | 2299 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| Flexural Modulus | 15.85 GPa | 2299 ksi | ASTM D790 |
| Izod Impact, Notched | 0.710 J/cm | 1.33 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.07 J/cm | 9.50 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 23.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C @Thickness 3.20 mm |
412 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 - 1.00e+11 ohm-cm | 1.00e+10 - 1.00e+11 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyMirae Moplen HP600R Injection Grade Polypropylene
- Fujipoly Industries Sarcon® 20GTR Thin-Film GTR
- LATI Latigray 82-04 CX/90 PA 12
- Shinil Chemical SHINNANO PA-66 Polymer Nanocomposite CHC
- TIMCAL TIMREX® M150 mesh FR Natural Flake Graphite
- Dow Corning SILASTIC® LS 5-2060 FLUOROSILICONE RUBBER
- Epoxy Technology EPO-TEK® 353ND-T5 High Temperature Thixotropic Epoxy
- Fainplast Compounds GK 0474 Flexible PVC, Flame Retardant Sheathing Lead Free
- Axiall 6704 Moldings & Extrusions Flexible PVC
- DuPont Bynel® 41E558 Anhydride-Modified LLDPE Adhesive Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved