SABIC Innovative Plastics LNP STAT-KON DE004 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE004 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DE004 is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00040 - 0.00090 cm/cm @Time 86400 sec |
0.00040 - 0.00090 in/in @Time 24.0 hour |
ISO 294 |
| 0.00040 - 0.0010 cm/cm @Time 86400 sec |
0.00040 - 0.0010 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0040 cm/cm @Time 86400 sec |
0.0030 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0037 - 0.0045 cm/cm @Time 86400 sec |
0.0037 - 0.0045 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 114 MPa | 16500 psi | ISO 527 |
| 120 MPa | 17400 psi | ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Tensile Modulus | 10.6 GPa | 1540 ksi | 1 mm/min; ISO 527 |
| 10.89 GPa | 1579 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 188 MPa | 27300 psi | ISO 178 |
| 196 MPa | 28400 psi | ASTM D790 | |
| Flexural Modulus | 9.78 GPa | 1420 ksi | ISO 178 |
| 9.79 GPa | 1420 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.730 J/cm | 1.37 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.90 J/cm | 9.18 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J | 11.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 13.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
7.39 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 14.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
7.78 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 42.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 42.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 144 °C | 291 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 10000 ohm | 10 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polymer Resources PPX-FR1 Modified-PPO, V-0 Flame Retardant
- Premix Thermoplastics PRE-ELEC® CP 1315 (discontinued **)
- DuPont Performance Polymers Delrin® FG400XRD NC010 Acetal (Unverified Data**)
- Solvay Specialty Polymers Algoflon® L206 Polytetrafluoroethylene (PTFE) (Unverified Data**)
- Kinlead PT21 Adhesive Tape Grade BOPP Plain Film (thickness: 60 µm)
- Plenco 3509 Phenolic, Granular, Transfer Molded
- Wellman Wellamid® 22LH-N Unfilled Nylon 66, Lubricated & Heat Stabilized
- A. Schulman POLYBATCH™ White LL8855 GP Concentrate Based In LLDPE
- ExxonMobil HDPE HD 6909.65 High Density Polyethylene Copolymer Resin
- ArcelorMittal 51 High formability steel for drawing, Cold rolled
Copyright © lookpolymers.com All Rights Reserved