Renegade Materials Corporation RM-5003 Cyanate Ester Prepreg 4581 Quartz Fabric

Category Polymer , Thermoset , Filled/Reinforced Thermoset
Manufacturer Renegade Materials Corporation
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Renegade Materials Corporation RM-5003 Cyanate Ester Prepreg 4581 Quartz Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low dielectric and loss, high performance prepreg. 350°F Cure Developed with consistent handling and superior performance Designed for demanding electrical, radome and antennae applications Delivers superior performance with service up to 350°F with post cure Available in woven and unidirectional product forms using all fibers including carbon, quartz and S2 glass Nano-enhancement for tailored laminate properties and multi-functional performanceInformation provided by Renegade Materials Corporation.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Resin
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 876 MPa
127000 psi
Prepreg, RT, Dry; ASTM D3039
Elongation at Break 4.5 %
4.5 %
Resin, RT, Dry
Tensile Modulus 26.2 GPa
3800 ksi
Prepreg, RT, Dry
Flexural Strength 138 MPa
20000 psi
Resin
993 MPa
144000 psi
Prepreg, RT, Dry; ASTM D6272
Flexural Modulus 3.65 GPa
530 ksi
Resin
26.9 GPa
3900 ksi
Prepreg, RT, Dry
Compressive Strength 621 MPa
90000 psi
0°, 90° Directions, RT, Dry; ASTM D6641
Shear Strength 82.7 MPa
12000 psi
Short Beam Shear, 0° Direction, RT, Dry; ASTM D2344
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 166 °C
331 °F
Prepreg, Measured from Storage Modulus, Wet
190 °C
374 °F
Prepreg, Measured from Storage Modulus, Dry
Electrical Properties Metric English Comments
Dielectric Constant 2.95

@Frequency 1.00e+10 Hz
2.95

@Frequency 1.00e+10 Hz
Dissipation Factor 0.0030

@Frequency 1.00e+10 Hz
0.0030

@Frequency 1.00e+10 Hz
Descriptive Properties Value Comments
Vf, Fiber Volume Fraction 55%
RT, Dry