Chi Mei Polylac® PA-757 ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Chi Mei Corporation (ChiMei)
Trade Name Polylac®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chi Mei Polylac® PA-757 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High gloss, medium impact
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0030 - 0.0070 cm/cm
0.0030 - 0.0070 in/in
ASTM D955
Melt Flow 1.8 g/10 min

@Load 5.00 kg,
Temperature 200 °C
1.8 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
22 g/10 min

@Load 10.0 kg,
Temperature 220 °C
22 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO-1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 116
116
ASTM D785
Ball Indentation Hardness 110 MPa
16000 psi
H358/30; ISO 2039-1
Tensile Strength at Break 37.0 MPa
5370 psi
50 mm/min; ISO 527
Tensile Strength, Yield 54.0 MPa
7830 psi
50 mm/min; ISO 527
Elongation at Break 20 %
20 %
50 mm/min; ISO 527
Flexural Strength 76.0 MPa
11000 psi
2 mm/min; ISO 178
Flexural Modulus 2.20 GPa
319 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.83 J/cm

@Thickness 6.35 mm
3.43 ft-lb/in

@Thickness 0.250 in
ASTM D256
2.05 J/cm

@Thickness 3.17 mm
3.84 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
ISO 180/1C
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
ISO 179
Impact 11.0
11.0
Impact Flexural Test Notched (KJ/m²)
NB
NB
Impact Flexural Test Unnotched (KJ/m²)
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
unannealed; ISO 75
98.0 °C
208 °F
annealed; ISO 75
Vicat Softening Point 100 °C

@Load 5.00 kg
212 °F

@Load 11.0 lb
50°C/hr; ISO 306
101 °C

@Load 5.00 kg
214 °F

@Load 11.0 lb
120°C/hr; ISO 306
104 °C

@Load 1.00 kg
219 °F

@Load 2.20 lb
50°C/hr; ISO 306
105 °C

@Load 1.00 kg
221 °F

@Load 2.20 lb
120°C/hr; ISO 306
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
UL 94