Polymer Resources PC/TP-GP2 PC/Polyester Alloy

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC/TP-GP2 PC/Polyester Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Impact, Excellent Chemical ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Linear Mold Shrinkage 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
Flow; ASTM D955
0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
Across Flow; ASTM D955
Melt Flow 6.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 265 °C
6.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 509 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.3 MPa
7300 psi
ASTM D638
Tensile Strength, Yield 51.7 MPa
7500 psi
ASTM D638
Flexural Strength 74.5 MPa
10800 psi
ASTM D790
Flexural Modulus 2.07 GPa
300 ksi
ASTM D790
Izod Impact, Notched 4.27 J/cm

@Temperature -40.0 °C
8.00 ft-lb/in

@Temperature -40.0 °F
ASTM D256
8.54 J/cm

@Temperature 22.8 °C
16.0 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Gardner Impact 36.2 J
26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 98.9 °C
210 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 93.3 °C
200 °F
ASTM D648
UL RTI, Electrical 75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
UL 746
75.0 °C

@Thickness 3.00 mm
167 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
UL 746
75.0 °C

@Thickness 3.00 mm
167 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
UL 746
75.0 °C

@Thickness 3.00 mm
167 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 9.50e+16 ohm-cm
9.50e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 249 - 271 °C
480 - 520 °F
Middle Barrel Temperature 254 - 277 °C
490 - 530 °F
Front Barrel Temperature 260 - 282 °C
500 - 540 °F
Melt Temperature 246 - 274 °C
475 - 525 °F
Mold Temperature 65.6 - 87.8 °C
150 - 190 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Descriptive Properties Value Comments
Vent 0.0015