Polyplastics Freqtis® P0813A (PPS/LCP), Molding Compound

Category	Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS); Molded
Manufacturer	Polyplastics Co.
Trade Name	Freqtis®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polyplastics Freqtis® P0813A (PPS/LCP), Molding Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Both base resins (PPS and LCP) exhibit excellent heat resistance, dimensional stability and molding processability. Therefore Freqtis® is widely used for surface mounted electronic components. In addition, these compounds have characteristics appropriate for high-frequency device materials on account of their low dielectric losses in high frequency regions.FREQTIS® molding compounds allow dielectric constant control through compounding with a high dielectric constant ceramic developed independently by Otsuka Chemical.p>Information provided by PolyPlastics.

Physical Properties	Metric	English	Comments
Density	2.13 g/cc	0.0770 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Flexural Strength	130 MPa	18900 psi	Flexural Strain: 0.7%; ISO 178
Flexural Modulus	21.0 GPa	3050 ksi	ISO 178

Thermal Properties	Metric	English	Comments
CTE, linear	20.0 µm/m-°C @Temperature 20.0 °C	11.1 µin/in-°F @Temperature 68.0 °F	ISO 11359-2
CTE, linear, Transverse to Flow	30.0 µm/m-°C @Temperature 20.0 °C	16.7 µin/in-°F @Temperature 68.0 °F	ISO 11359-2
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in

Electrical Properties	Metric	English	Comments
Dielectric Constant	8.0 @Frequency 1e+6 Hz	8.0 @Frequency 1e+6 Hz	Volumetric method
Dissipation Factor	0.0020 @Frequency 3.00e+9 Hz	0.0020 @Frequency 3.00e+9 Hz	Perturbation method by cavity resonator