- Multibase Multi-Flex® TPE A 5521 BLK
Multibase Multi-Flex® TPE A 5521 BLK
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® TPE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® TPE A 5521 BLK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TPE A 5521 is based on Shell's Kraton technology licensed to Multibase. The product is extensively used in automotive and non-automotive applications. Multi-Flex TPE contains Kratonâ„¢ G.Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | (Condition L) ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 55 | 55 | 10 sec; ASTM D-2240 |
| Tensile Strength, Ultimate | 5.20 MPa | 754 psi | ASTM D412 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D412 |
| Tear Strength | 19.3 kN/m | 110 pli | ASTM D624 |
| Compression Set | 16 % | 16 % | for 70 hours at 23°C; ASTM 395 |
| 47 % @Temperature 70.0 °C |
47 % @Temperature 158 °F |
for 70 hours at 70°C; ASTM 395 | |
| 70 % @Temperature 100 °C |
70 % @Temperature 212 °F |
70 hours at 100°C; ASTM 395 |