Lavergne VYTEEN PC 135 General Purpose Medium Viscosity Polycarbonate

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer	Lavergne Performance Compounds
Trade Name	VYTEEN
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lavergne VYTEEN PC 135 General Purpose Medium Viscosity Polycarbonate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Vyteen PC 135, Black, medium viscosity polycarbonate, has an excellent balance of stiffness and impact resistanceFeatures: - High heat resistance - Good processabilityInformation provided by Bieglo Gmbh for Lavergne Performance Compounds

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/inÂ³	ASTM D792
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	3.2 mm; ASTM D955
Melt Flow	12 g/10 min @Load 1.20 kg, Temperature 300 Â°C	12 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	5 mm/min; ASTM D638
Flexural Strength	100 MPa	14500 psi	1.3 mm/min; ASTM D790
Flexural Modulus	2.30 GPa	334 ksi	1.3 mm/min; ASTM D790
Izod Impact, Notched	7.00 J/cm @Temperature 23.0 Â°C	13.1 ft-lb/in @Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	120 Â°C	248 Â°F	ASTM D648

Processing Properties	Metric	English
Feed Temperature	255 - 270 Â°C	491 - 518 Â°F
Middle Barrel Temperature	265 - 280 Â°C	509 - 536 Â°F
Front Barrel Temperature	275 - 295 Â°C	527 - 563 Â°F
Nozzle Temperature	275 - 295 Â°C	527 - 563 Â°F
Melt Temperature	275 - 295 Â°C	527 - 563 Â°F
Mold Temperature	65.0 - 95.0 Â°C	149 - 203 Â°F
Injection Pressure	69.0 - 138 MPa	10000 - 20000 psi