Fujipoly Industries Sarcon® 45Q Thin-Film QR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 45Q Thin-Film QR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon QR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 55
55
ASTM D2240
60
60
60°C for 500 hrs with 95% RH; ASTM D2240
69
69
150°C for 1,000 hrs; ASTM D2240
82
82
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 2.22 MPa
322 psi
2.88 MPa
418 psi
60°C for 500 hrs with 95% RH
4.44 MPa
644 psi
150°C for 1,000 hrs
5.55 MPa
805 psi
200°C for 1,000 hrs
Elongation at Yield 77 %
77 %
200°C for 1,000 hrs
117 %
117 %
183 %
183 %
60°C for 500 hrs with 95% RH
250 %
250 %
Tear Strength 0.600 kN/m
3.42 pli
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.90e+14 ohm-cm
1.90e+14 ohm-cm
60°C for 500 hrs with 95% RH
1.00e+15 ohm-cm
1.00e+15 ohm-cm
4.30e+15 ohm-cm
4.30e+15 ohm-cm
150°C for 1,000 hrs
6.50e+15 ohm-cm
6.50e+15 ohm-cm
200°C for 1,000 hrs
Dielectric Constant 4.15

@Frequency 1e+6 Hz
 4.15

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
4.16

@Frequency 1000 Hz
 4.16

@Frequency 1000 Hz
 After 1000 hrs at 150°C
4.18

@Frequency 50 Hz
 4.18

@Frequency 50 Hz
 After 1000 hrs at 150°C
4.2

@Frequency 1e+6 Hz
 4.2

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
4.22

@Frequency 1000 Hz
 4.22

@Frequency 1000 Hz
 After 1000 hrs at 200°C
4.23

@Frequency 1e+6 Hz
 4.23

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
4.23

@Frequency 1e+6 Hz
 4.23

@Frequency 1e+6 Hz
4.24

@Frequency 50 Hz
 4.24

@Frequency 50 Hz
 After 1000 hrs at 200°C
4.24

@Frequency 1000 Hz
 4.24

@Frequency 1000 Hz
4.27

@Frequency 1000 Hz
 4.27

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
4.3

@Frequency 50 Hz
 4.3

@Frequency 50 Hz
4.34

@Frequency 50 Hz
 4.34

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
Dielectric Strength 8.00 kV/mm
203 kV/in
AC 60 Hz
12.0 kV/mm
305 kV/in
150°C for 1,000 hrs
12.0 kV/mm
305 kV/in
60°C for 500 hrs with 95% RH
13.0 kV/mm
330 kV/in
200°C for 1,000 hrs
Dielectric Breakdown 8000 V
8000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.0017

@Frequency 1e+6 Hz
 0.0017

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.0020

@Frequency 1e+6 Hz
 0.0020

@Frequency 1e+6 Hz
0.0022

@Frequency 1e+6 Hz
 0.0022

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
0.0023

@Frequency 1000 Hz
 0.0023

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.0026

@Frequency 1e+6 Hz
 0.0026

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
0.0028

@Frequency 50 Hz
 0.0028

@Frequency 50 Hz
 After 1000 hrs at 200°C
0.0028

@Frequency 1000 Hz
 0.0028

@Frequency 1000 Hz
 After 1000 hrs at 200°C
0.0031

@Frequency 50 Hz
 0.0031

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.0035

@Frequency 1000 Hz
 0.0035

@Frequency 1000 Hz
0.0058

@Frequency 50 Hz
 0.0058

@Frequency 50 Hz
0.0069

@Frequency 1000 Hz
 0.0069

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
0.0136

@Frequency 50 Hz
 0.0136

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
Descriptive Properties Value Comments
Color Grey
Thermal Impedance 0.77°C/W
FTM P-3010; ASTM D5470