Fibre Glast Saf-T-Poxy 2410 / 2183 Epoxy (discontinued **)
| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fibre Glast Saf-T-Poxy 2410 / 2183 Epoxy
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Fibre Glast Developments Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | |
| Viscosity | 1300 cP | 1300 cP | ASTM D2293 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 88 | 88 | Cured; ASTM D2240 |
| Tensile Strength at Break | 270.8 MPa | 39280 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Elongation at Break | 1.83 % | 1.83 % | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Tensile Modulus | 14.9 GPa | 2160 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content. |
| Flexural Strength | 323.06 MPa | 46856 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Flexural Modulus | 16.6 GPa | 2410 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 84.4 °C | 184 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Pot Life | 120 min @Temperature 25.0 °C |
120 min @Temperature 77.0 °F |
4 fl. Oz.; ASTM D2471 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mix Ratio | 100:44 | Resin:Hardener by Weight |
| 2.13:1 | Resin:Hardener by Volume |
Users viewing this material also viewed the following:
- Overview of materials for PEN-PET
- LG Chemical Toluene
- Samsung Cheil Industries Infino® NH-3402F PC, 40% Glass Filled FR
- A. Schulman PP 1247-01 Polypropylene Homopolymer Polypropylene
- Dow Corning HV 1660/65 LIGHT GRAY SILICONE RUBBER KP
- Dow Nordel® IP 4725P Dense Extrusion
- Barlog Plastics KEBAFORM C 8027 POM Copolymer, 30% mineral reinforced
- Bhansali Engineering Santron IMS 2007LF SAN Resin
- Reade Advanced Materials Sillimanite Powder & Crystal (Al2SiO5)
- Sylvin Technologies 9604-95C Clear PVC for Injection Molding
Copyright © lookpolymers.com All Rights Reserved