ExxonMobil LD 617.LN Molding, Extrusion and Compounding Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Molded
Manufacturer	Exxon Chemical
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LD 617.LN Molding, Extrusion and Compounding Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 617.LN is a high flow, low density polyethylene homopolymer resin designed to provide excellent processability, flexibility and surface appearance. This multipurpose resin is performance engineered for applications such as housewares, overcaps and closures and concentrates.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: NoApplications: CapsClosuresCompoundingFood Packaging ContainersHouseware ArticlesInjection MoldingLabwareMasterbatch Base Resin Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.919 g/cc	0.0332 lb/in³	ExxonMobil Method
Melt Flow	26 g/10 min @Load 2.16 kg, Temperature 190 °C	26 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	86	86	15s; ASTM D2240
Hardness, Shore D	42	42	15s; ASTM D2240
Tensile Strength at Break	7.58 MPa	1100 psi	ASTM D638
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Elongation at Break	120 %	120 %	ASTM D638
Elongation at Yield	30 %	30 %	ASTM D638
1% Secant Modulus	234 MPa	34000 psi	ASTM D790
Impact Test	16.3 J	12.0 ft-lb	@ 73ºF, Instrumented Impact Total Energy; ASTM D3763
	19.0 J @Temperature -20.0 °C	14.0 ft-lb @Temperature -4.00 °F	Instrumented Impact Total Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	110 °C	230 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	83.9 °C	183 °F	ASTM D1525