ExxonMobil Exact™ 3040 Cast Ethylene-based Plastomer Resin
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Exxon Chemical |
| Trade Name | EXACT™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Exact™ 3040 Cast Ethylene-based Plastomer Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Exact 3040 is an ethylene-based hexane copolymer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. Exact 3040 is designed for monolayer and coextrusion cast film extrusion coating, and extrusion laminating applications. Typical applications include seal layers for packaging films. Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: NoInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ExxonMobil method |
| Melt Flow | 17 g/10 min | 17 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 5.17 MPa | 750 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 4.55 MPa | 660 psi | ASTM D882 |
| Film Elongation at Break, MD | 610 % | 610 % | ASTM D882 |
| Film Elongation at Break, TD | 770 % | 770 % | ASTM D882 |
| Secant Modulus, MD | 0.0689 GPa | 10.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.0758 GPa | 11.0 ksi | ASTM D882 |
| Puncture Energy | 5.42 J | 4.00 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 330 g | 330 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 530 g | 530 g | ASTM D1922 |
| Dart Drop Test | 100 g | 0.221 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 55.2 MPa | 8000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 46.9 MPa | 6800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 203 °C | <= 397 °F | Peak Melting Point; ExxonMobil method |
| Crystallization Temperature | <= 174 °C | <= 345 °F | Peak; ExxonMobil Method |
| Vicat Softening Point | 77.2 °C | 171 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 0.30 % | 0.30 % | ASTM D1003 |
| Gloss | 93 % | 93 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Force | 11 lbf | ExxonMobil Method |