ExxonMobil ESCOR™ AT 310 Molding, extrusion and compounding resin (discontinued **)

Category	Polymer , Thermoplastic , Ethylene Acrylic Acid , Ethylene Methyl Acrylate
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil ESCOR™ AT 310 Molding, extrusion and compounding resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ESCOR AT 310 provides excellent adhesion to a variety of polar and non-polar materials such as metals, glass, polyolefins, polyamides, polyesters, etc. It is suitable for use as a polymer modifier to improve bonding and toughness.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.942 g/cc	0.0340 lb/in³	ExxonMobil Method
Methyl Acrylate Content	6.5 %	6.5 %
Acrylic Acid Content	6.5 %	6.5 %
Melt Flow	6.0 g/10 min	6.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	85	85	15s; ASTM D2240
Hardness, Shore D	35	35	15s; ASTM D2240
Tensile Strength at Break	12.4 MPa	1800 psi	ASTM D638
Elongation at Break	700 %	700 %	ASTM D638
Flexural Modulus	0.0427 GPa	6.20 ksi	1% secant; ASTM D790
Impact Test	28.5 J @Temperature 23.0 °C	21.0 ft-lb @Temperature 73.4 °F	Instrument Impact, Total Energy; ASTM D3763
	33.9 J @Temperature -40.0 °C	25.0 ft-lb @Temperature -40.0 °F	Instrumented Impact, Total Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	86.1 °C	187 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	60.0 °C	140 °F	ASTM D1525

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer