DuPont Teijin Films Melinex® 523 Polyester Film

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Melinex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Melinex® 523 Polyester Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Melinex® 523 is a high clarity polyester film. It is pretreated on both surfaces with MAP (multiple application pretreatment) to promote adhesion to most aqueous and solvent coating formulations. Intended for use in applications where thermal stability and adhesion properties are key requirements.Information provided by DuPont.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 89.6 MPa
13000 psi
ASTM D882A
Film Tensile Strength at Yield, TD 89.6 MPa
13000 psi
ASTM D882A
Film Elongation at Break, MD 200 %
200 %
ASTM D882A
Film Elongation at Break, TD 120 %
120 %
ASTM D882A
Coefficient of Friction, Static 0.40 - 0.50
0.40 - 0.50
ASTM D1894
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
Film Tensile Strength at Break, TD 172 MPa
25000 psi
ASTM D882A
Thermal Properties Metric English Comments
Shrinkage, MD 1.0 %

@Temperature 190 °C,
Time 300 sec
1.0 %

@Temperature 374 °F,
Time 0.0833 hour
Unrestrained
Shrinkage, TD 0.80 %

@Temperature 190 °C,
Time 300 sec
0.80 %

@Temperature 374 °F,
Time 0.0833 hour
Unrestrained
Optical Properties Metric English Comments
Transmission, Visible 87 %

@Thickness 0.178 mm
87 %

@Thickness 0.00700 in
TLT; ASTM D1003
88 %

@Thickness 0.0965 mm
88 %

@Thickness 0.00380 in
TLT; ASTM D1003
88 %

@Thickness 0.102 mm
88 %

@Thickness 0.00400 in
TLT; ASTM D1003
88 %

@Thickness 0.127 mm
88 %

@Thickness 0.00500 in
TLT; ASTM D1003
89 %

@Thickness 0.0673 mm
89 %

@Thickness 0.00265 in
TLT; ASTM D1003
89 %

@Thickness 0.0762 mm
89 %

@Thickness 0.00300 in
TLT; ASTM D1003