Polymer Property : Film Tensile Strength at Break, TD = 25000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	172 MPa	25000 psi	20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 28UBW-ES OPP Film Product Description: A multi-layer, cavitaed, white OPP film with an enhanced sealant to allow sealing through contamination. This film has an exceptional barrier to gases, flavors, and moisture. It..
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 054 Polyester Film Melinex® 054 is a high clarity, low balanced shrink polyester film which is two-side pretreated to promote adhesion to industrial coatings and inks.Information provided by DuPont.
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 359 Polyester Film, 1000 Gauge Melinex® 359 is a white opaque polyester film with a two side chemical pre-treatment for improved ink adhesion and laser printing.Information provided by DuPont.
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 359 Polyester Film, 500 Gauge Melinex® 359 is a white opaque polyester film with a two side chemical pre-treatment for improved ink adhesion and laser printing.Information provided by DuPont.
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 359 Polyester Film, 700 Gauge Melinex® 359 is a white opaque polyester film with a two side chemical pre-treatment for improved ink adhesion and laser printing.Information provided by DuPont.
Film Tensile Strength at Break, TD	>= 172 MPa	>= 25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 461 Polyester Film Melinex® 461 is a high clarity polyester film manufactured with a coating on one surface that promotes adhesion to many solvent formulations and to most vinyl or acrylic base ink systems. The adhes..
Film Tensile Strength at Break, TD	>= 172 MPa	>= 25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 473 Polyester Film, 200 Gauge Melinex® 473 is a high clarity polyester film manufactured with a coating on one surface that improves slip and handling characteristics. The opposite surface is raw polyester (non-coated). The sli..
Film Tensile Strength at Break, TD	>= 172 MPa	>= 25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 478 Polyester Film, 200 Gauge Melinex® 478 is a high clarity polyester film manufactured with a coating on both surfaces that improves slip and handling characteristicsTypical Applications: Melinex 478 is used in many general i..
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® A Polyester Film, 1400 Gauge Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, ..
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® EL21 Polyester Film, 1400 Gauge Mylar® EL21 polyester films are flexible strong and durable films with an unusual balance of properties, making them suitable for a variety of industrial applications. The excellent dielectric stre..
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® MDA Polyester Film, 1400 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion..
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® MO21 Polyester Film, 1400 Gauge Product Description: Mylar® type MO21 films are strong, heavy gauge films that have excellent electrical properties. These films offer exceptional cut-through resistance, low shrinkage, low moistur..
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 340 Polyester Film, 200 Gauge Melinex® 340 is an opaque white polyester film with good handling properties that is not treated on either surface.Typical Applications: Melinex® 340 is used as a base for pressure sensitive label..
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 523 Polyester Film Melinex® 523 is a high clarity polyester film. It is pretreated on both surfaces with MAP (multiple application pretreatment) to promote adhesion to most aqueous and solvent coating formulations. I..
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® WLB Polyester Film, 500 Gauge Melinex® WLB is a polyester film with a white surface, a light grey surface and very high opacity. General Product Info: Melinex® WLB offers a film with a white surface and very high opacity. It c..
Film Tensile Strength at Break, TD	172 MPa	25000 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 30MW747 OPP Film Product Description: White opaque biaxially oriented polypropylene film coated on one side acrylic, one side PVdC. Provides excellent performances on all packaging machines. 30MW747 is a super white..
Film Tensile Strength at Break, TD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 343 Polyester Film, 200 Gauge Melinex® 343 is an opaque white polyester film with good handling properties that is treated on one surface to promote adhesion to most industrial coatings.Typical Applications: Melinex® 343 is us..