Polymer Property : Film Tensile Strength at Break, MD = 20000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor® 100 LTSC OPP Film
Product Description: Bicor LTSC is a two-side coated OPP film which is designed for use in high-speed or demanding horizontal, fin seal, packaging applications. The low-temperature seal coating (LTS..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor® 220 AB OPP Film
Product Description: Bicor AB is a two-side acrylic coated, sealable OPP film designed for general use in overwrap and horizontal packaging. It can be surface printed, reverse printed, or used unpri..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor® 380 AB OPP Film
Product Description: Bicor AB is a two-side acrylic coated, sealable OPP film designed for general use in overwrap and horizontal packaging. This film is suitable as an unsupported web or lamination..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor® 420 HS OPP Film
Product Description: Bicor HS is a two-side coated, sealable OPP film designed for general use in overwrap and horizontal packaging. This film is suitable as an unsupported web or lamination. It can..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor® 85 LTSC OPP Film
Product Description: Bicor LTSC is a two-side coated OPP film which is designed for use in high-speed or demanding horizontal, fin seal, packaging applications. The low-temperature seal coating (LTS..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 70 MB OPP Film
Product Description: Bicor 70 MB is a biaxially oriented polypropylene film for use in metalized film applications. 70 MB, when metalized, is used in adhesive and extrusion laminations to reveres-pr..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 70 SLP OPP Film
Product Description: Bicor 70 SLP is a one-side treated, non-heat sealable OPP film designed for use as the outside web of a lamination. The treated print surface is intended as the print and lamina..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte® 18 LLG-101 Clear OPP Film
Product Description: A clear, one-side treated, polypropylene film that is designed to provide exceptional clarity and print protection when used as over laminates in pressure-sensitive labeling app..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
510
ExxonMobil Label-Lyte® 612 LLG-102 Clear OPP Film
Clear, polypropylene films designed for use in roll-fed labeling applications. This film can be laminated to itself or applied as an outer web to other films. The print surface is a treated high ene..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 18LL-101 OPP Film
Product Description: A clear, one-side treated, polypropylene film that is designed to provide exceptional clarity and print protection when used as overlaminates in pressure-sensitive labeling appl..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 612LLG102 OPP Film
Product Description: A clear, two-side treated, polypropylene film that is used in roll-fed labeling applications. This film can be laminated to itself or applied as an outer web to other films. 612..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® 054 Polyester Film
Melinex® 054 is a high clarity, low balanced shrink polyester film which is two-side pretreated to promote adhesion to industrial coatings and inks.Information provided by DuPont.
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® 3381 Polyester Film
Melinex® 3381 is a two-side heat sealable, opaque white polyester film which is ideal in specialty card laminate applications. This film can be heat sealed to itself and other polyesters, as well a..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® 359 Polyester Film, 500 Gauge
Melinex® 359 is a white opaque polyester film with a two side chemical pre-treatment for improved ink adhesion and laser printing.Information provided by DuPont.
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® 359 Polyester Film, 700 Gauge
Melinex® 359 is a white opaque polyester film with a two side chemical pre-treatment for improved ink adhesion and laser printing.Information provided by DuPont.
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® 534 Polyester Film, 380 Gauge
Melinex® 534 is an opaque white film with superb handling properties and a unique glossy appearance. It is pre-treated on both surfaces to promote adhesion to aqueous based inks and coatings.Inform..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® 565 Polyester Film
Melinex® 565 is a high clarity film which is differentially coated. One surface is coated with the standard T-Sub adhesion promoter; the opposite surface is coated for antistatic protection.Informa..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® ST339 Polyester Film, 1000 Gauge
Melinex® ST339 is a stabilized, opaque white polyester film with good handling and lay flat properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings Typical A..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® ST339 Polyester Film, 300 Gauge
Melinex® ST339 is a stabilized, opaque white polyester film with good handling and lay flat properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings Typical A..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® ST339 Polyester Film, 380 Gauge
Melinex® ST339 is a stabilized, opaque white polyester film with good handling and lay flat properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings Typical A..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® ST339 Polyester Film, 500 Gauge
Melinex® ST339 is a stabilized, opaque white polyester film with good handling and lay flat properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings Typical A..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Melinex® ST339 Polyester Film, 700 Gauge
Melinex® ST339 is a stabilized, opaque white polyester film with good handling and lay flat properties that is pre-treated on both surfaces to promote adhesion to most industrial coatings Typical A..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Mylar® EB31 Polyester Film, 200 Gauge
Mylar® EB31 is a smooth, matte polyester film. It does not contain any plasticizers. General Product Info: Mylar® EB31 has low haze and intermediate gloss. This offers more realistic colors and cl..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882A
DuPont Teijin Films Mylar® EB31 Polyester Film, 92 Gauge
Mylar® EB31 is a smooth, matte polyester film. It does not contain any plasticizers. General Product Info: Mylar® EB31 has low haze and intermediate gloss. This offers more realistic colors and cl..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ExxonMobil Method
ExxonMobil Bicor® 110 ASB-X OPP Film
Product Description: Bicor ASB-X is a two side coated, sealable OPP film designed for broad use in many applications, including overwrap, horizontal, and vertical packaging. ASB-X is good for heavy ..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor® 120 LTSC OPP Film
Product Description: Bicor LTSC is a two-side coated OPP film which is designed for use in high-speed or demanding horizontal, fin seal, packaging applications. The low-temperature seal coating (LTS..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 25 ARW OPP Film
Product Description: Bicor ARW is a two-side acrylic-coated OPP film designed for use in lamination and monoweb applications, especially for paper ream wrap. The acrylic-coated side with the higher ..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
ASTM D882
Honeywell MAP-Shield™ AF Generation 2 Shrinkable Barrier Film  (discontinued **)
Description: MAP-Shield™ AF shrinkable barrier film is ideal for modified atmosphere packaged (MAP) food products in barrier trays for extended shelf life protection. The coextruded, biaxially orie..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
510
ExxonMobil Bicor® 120 LCX OPP Film
One-side treated, one-side sealable OPP film designed for use in a lamination. It is typically laminated to Metallyte, HBS-2, SPW, and itself to create lap sealable packages. The high energy surfac..
Film Tensile Strength at Break, MD 138 MPa
20000 psi
510
ExxonMobil Label-Lyte® 612 LL-112 Clear OPP Overlaminate
Clear, polypropylene film designed to provide exceptional clarity and print protection when used as an overlaminate in pressure-sensitive labeling applications. The treated high energy layer provide..