DuPont Performance Polymers Rynite® RE5264 NC010 PET (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Rynite® RE5264 NC010 PET
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Rynite® RE5264 NC010 is a 36% glass fiber reinforced, color stabilized, modified polyethylene terephthalate.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in³ | ISO 1183 |
| Filler Content | 36 % | 36 % | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm |
0.0030 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm |
0.0080 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Melt Index of Compound | 27 g/10 min @Load 5.00 kg, Temperature 280 °C |
27 g/10 min @Load 11.0 lb, Temperature 536 °F |
cm3/10 min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 207 MPa @Temperature 23.0 °C |
30000 psi @Temperature 73.4 °F |
ISO 527 |
| Elongation at Break | 2.4 % @Temperature 23.0 °C |
2.4 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 14.0 GPa @Temperature 23.0 °C |
2030 ksi @Temperature 73.4 °F |
ISO 527 |
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 246 °C | 475 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 21.5 kV/mm @Temperature 23.0 °C |
546 kV/in @Temperature 73.4 °F |
IEC 60243-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| 280 °C | 536 °F | Optimum | |
| Mold Temperature | >= 130 °C | >= 266 °F | |
| 140 °C | 284 °F | optimum | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | <= 0.010 % | <= 0.010 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Drying Recommended | Yes | |
| Filler | Glass fiber | |
| Forms | Pellets | |
| Generic | PET | |
| Material Status | Preliminary Data | |
| Processing Method | Injection Molding | |
| Product Category | Color Stable Resins | |
| Glass Reinforced Resins | ||
| Region Available - Global | Yes | |
| RoHS Compliance | Contact Manufacturer |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXE124R PC (Europe-Africa-Middle East)
- Hong Kun Group CDI Pharmaceutical Intermediate
- Lord Adhesives 7542D Two-Component Urethane Adhesive
- Lanxess Pocan® DP 4035 000000 PBT + PET, 30% Glass Fiber
- Lucent Polymers PC-1410 Polycarbonate, Injection/Extrusion Grade
- LG Chemical 95HCTC SAN, High Transparency, Heat Resistance, Chemical Resistance
- Silberline Sparkle Silvex® 965-30-D
- DuPont Performance Polymers Rynite® FR543 NC010 PET
- Clariant Renol 60G33-L Nylon 6, 33% Glass Fiber Reinforced, Lubricated
Copyright © lookpolymers.com All Rights Reserved