Dow SE SLR-6410 Solution polymerized Styrene Butadiene Rubber (S-SBR)

Category Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer Dow Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow SE SLR-6410 Solution polymerized Styrene Butadiene Rubber (S-SBR).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SE SLR-6410 is manufactured by anionic solution polymerization using lithium initiator and is extended with 50 parts of aromatic oil in relation to solid rubber. It is a product with medium styrene and high vinyl content. The product is partially Sn-coupled and non-staining stabilized. SE SLR-6410 is widely used in the tire industry for the manufacture of high performance summer tires providing an excellent grip and dry handling behavior. It can also be used for the manufacture of high-quality technical rubber articles. It is supplied in bales weighing 25 kg. Bales are wrapped in 50 micron PE film. At mixing temperatures above 110°C, the rubber can be processed with the packaging film. Information provided by Dow
Physical Properties Metric English Comments
Viscosity Measurement 3.8

@Temperature 160 °C
3.8

@Temperature 320 °F
[dNm]; ML, (0.5 RAD); ASTM D5289
5.0

@Temperature 160 °C
5.0

@Temperature 320 °F
[min]; ts1, (0.5 RAD); ASTM D5289
8.5

@Temperature 160 °C
8.5

@Temperature 320 °F
[min]; T50, (0.5 RAD); ASTM D5289
12.5

@Temperature 160 °C
12.5

@Temperature 320 °F
[min]; T90, (0.5 RAD); ASTM D5289
14.7

@Temperature 160 °C
14.7

@Temperature 320 °F
[dNm]; MH, (0.5 RAD); ASTM D5289
Mooney Viscosity 65

@Temperature 100 °C
65

@Temperature 212 °F
[MU]; ML 1+4, unmassed sample; ASTM D1646
Vinyl Acetate Content 25 %
25 %
FTIR, internal method
Collected Volatile Condensable Material 0.34 %
0.34 %
ASTM D5668
Storage Temperature <= 30.0 °C
<= 86.0 °F
Mechanical Properties Metric English Comments
Hardness, Shore A 57

@Thickness 12.5 mm
57

@Thickness 0.492 in
(25 min / 160°C); ASTM D2240
Tensile Strength, Ultimate 23.0 MPa
3340 psi
Die C (35 min / 145°C); ASTM D412
Tensile Strength, Yield 9.00 MPa

@Strain 300 %
1310 psi

@Strain 300 %
ASTM D412
Elongation at Break 630 %
630 %
ASTM D412
Rebound 23 %

@Thickness 12.5 mm
23 %

@Thickness 0.492 in
Schob pendulum, (25 min / 160°C); ISO 4662
Thermal Properties Metric English Comments
Vicat Softening Point 92.2 °C
198 °F
Glass Transition Temp, Tg -32.9 °C
-27.2 °F
HR 10 K/min; half height; DSC
Chemical Properties Metric English Comments
Styrene Content 40 %
40 %
FTIR, internal method
Processing Properties Metric English Comments
Shelf Life >= 12.0 Month
>= 12.0 Month
Descriptive Properties Value Comments
Accelerator (TBBS) wt% 1.5
ASTM 3185-3B
Carbon Black wt% 75
ASTM 3185-3B; IRB 7
Stearic Acid wt% 1
ASTM 3185-3B
Sulfur content, % 1.75
ASTM 3185-3B
Total Extractables % 32.9
ASTM D5774
Zinc Oxide wt% 3
ASTM 3185-3B