3M 5010 Polyurethane Multi-Purpose Adhesive

Category Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Adhesive
Manufacturer 3M
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M 5010 Polyurethane Multi-Purpose Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Polyurethane Multi-Purpose Adhesive 5010 is a one component, fast curing adhesive which forms a rigid permanent bond. 3M 5010 bonds to a wide variety of materials including wood, foam panels, fiberglass, and wood.Information provided by 3M
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
Volatile Organic Compounds (VOC) Content 2.1 g/l
2.1 g/l
Mechanical Properties Metric English Comments
Tensile Strength at Break 1.90 MPa
276 psi
ASTM D412
100% Modulus 0.0117 GPa
1.70 ksi
ASTM D412
Shear Strength 0.352 MPa
51.0 psi
Overlap, Polypropylene
0.621 MPa
90.0 psi
Overlap, LD Polyethylene
1.81 MPa
262 psi
Overlap, Nylon
2.30 MPa
333 psi
Overlap, Glass
2.46 MPa
357 psi
Overlap, Polycarbonate
3.39 MPa
492 psi
Overlap, Acrylic
3.64 MPa
528 psi
Overlap, ABS
4.73 MPa
686 psi
Overlap, Fir
5.45 MPa
790 psi
Overlap, PVC
6.24 MPa
905 psi
Overlap, Aluminum
6.971 MPa
1011 psi
Overlap, Cold Rolled Steel
7.184 MPa
1042 psi
Overlap, Stainless Steel
11.50 MPa
1668 psi
Overlap, FRP Green
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 100 °C
212 °F
Minimum Service Temperature, Air -30.0 °C
-22.0 °F
Processing Properties Metric English Comments
Cure Time 3.00 - 5.00 min
0.0500 - 0.0833 hour
Open Time
30.0 min
0.500 hour
Pressing Time
1440 min
24.0 hour
Final Setting Time
Shelf Life 12.0 Month
12.0 Month