Dow 118.01 Developmental Performance Polypropylene Polymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Extrusion Grade , Polypropylene, Film Grade , Polypropylene, Molded , Polypropylene, Sheet/Thermoforming Grade
Manufacturer Dow Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow 118.01 Developmental Performance Polypropylene Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
D118.01 Developmental Performance Polymer is a propylene-based resin intended for use in film, sheet extrusion and injection molding applications. Film and sheet produced from this resin offer improved stiffness, heat resistance, machinability, and toughness over competitive cast polypropylene films. Coextruded structures offer a broad range of potentially improved properties including high stiffness, good clarity and barrier properties.Excellent balance of clarity and stiffnessSuperior stiffness and heat resistance over conventional polypropylenesSuggested for use in cast film applications requiring improved stiffness, barrier or heat resistanceSuggested for use in injection molded articles requiring stiffness of a 20% mineral filled PPComplies with U.S. FDA 21 CFR 177.1520(c) 1.1a, Europe EU-Directive 2002/72/ECDow Announced Sale of Global Polypropylene Business to Braskem in July 2011.
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ASTM D792
Thickness 25.4 microns
1.00 mil
Film Thickness
Melt Index of Compound 8.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 31.5 MPa
4570 psi
25.4 microns; ASTM D882
Film Tensile Strength at Yield, TD 30.4 MPa
4410 psi
25.4 microns; ASTM D882
Tensile Strength, Yield 42.1 MPa
6110 psi
ASTM D638
Film Elongation at Break, MD 530 %
530 %
25.4 microns; ASTM D882
Film Elongation at Break, TD 6.0 %
6.0 %
25.4 microns; ASTM D882
Flexural Modulus, 1% Secant 2280 MPa
331000 psi
ASTM D790A
Secant Modulus, MD 1.07 GPa
155 ksi
2% secant modulus; ASTM D882
Secant Modulus, TD 1.06 GPa
154 ksi
2% secant modulus; ASTM D882
Izod Impact, Notched 0.267 J/cm
0.500 ft-lb/in
ASTM D256A
Film Tensile Strength at Break, MD 55.5 MPa
8050 psi
25.4 microns; ASTM D882
Film Tensile Strength at Break, TD 30.4 MPa
4410 psi
25.4 microns; ASTM D882
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 129 °C
264 °F
Unannealed; ASTM D648
Optical Properties Metric English Comments
Haze 21 %
21 %
1000 microns; ASTM D1003