Material Notes:

AQUAMET 22 is a high-alloy stainless steel with superior corrosion resistance along with excellent toughness and high strength. It has higher strength than AQUAMET 17 in 3/4" to 1-1/4" dia., and it has equivalent in strength in 1-3/8" to 2" dia. Due to its high alloy content, AQUAMET 22 resists pitting and crevice corrosion and is ideal for pleasure boats which are operated infrequently, spending much of their time tied up at docks. AQUAMET 22 H.S. is a high strength version available in 2-1/2" - 6" dia. NOTE: The mechanical properties of AQUAMET 22 H.S. are slightly lower in sizes 5" dia. and over.Information provided by Crucible Specialty Metals.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	862 MPa @Thickness 127 - 152 mm	125000 psi @Thickness 5.00 - 6.00 in	Aquamet 22 HS
	1000 MPa @Thickness 19.0 - 31.8 mm	145000 psi @Thickness 0.750 - 1.25 in
Tensile Strength, Yield	414 MPa @Strain 0.200 %, Thickness 127 - 152 mm	60000 psi @Strain 0.200 %, Thickness 5.00 - 6.00 in	Tension; Aquamet 22 HS
	621 MPa @Strain 0.200 %, Thickness 127 - 152 mm	90000 psi @Strain 0.200 %, Thickness 5.00 - 6.00 in	Tension; Aquamet 22 HS
	896 MPa @Strain 0.200 %, Thickness 19.0 - 31.8 mm	130000 psi @Strain 0.200 %, Thickness 0.750 - 1.25 in	Tension
Elongation at Break	15 %	15 %	in 2"; 5" to 6"; Aquamet 22 HS
	18 %	18 %	in 2"; 3/4" to 1-1/4"
Reduction of Area	50 %	50 %	1-1/4" to 12"
	45 % @Thickness 19.0 - 31.8 mm	45 % @Thickness 0.750 - 1.25 in
Shear Strength	597 MPa @Strain 0.200 %, Thickness 19.0 - 31.8 mm	86600 psi @Strain 0.200 %, Thickness 0.750 - 1.25 in

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.060 %	<= 0.060 %
Chromium, Cr	20.5 - 23.5 %	20.5 - 23.5 %
Iron, Fe	>= 51.87 %	>= 51.87 %	As Remainder
Manganese, Mn	4.0 - 6.0 %	4.0 - 6.0 %
Molybdenum, Mo	1.5 - 3.0 %	1.5 - 3.0 %
Nb + Ta	0.10 - 0.30 %	0.10 - 0.30 %
Nickel, Ni	11.5 - 13.5 %	11.5 - 13.5 %
Nitrogen, N	0.20 - 0.40 %	0.20 - 0.40 %
Phosphorous, P	<= 0.040 %	<= 0.040 %
Silicon, Si	<= 1.0 %	<= 1.0 %
Sulfur, S	<= 0.030 %	<= 0.030 %
Vanadium, V	0.10 - 0.30 %	0.10 - 0.30 %