Lubrizol Advanced Materials PearlthaneÂ® ECO D12T90 Thermoplastic Polyurethane

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyurethane, TP
Manufacturer	Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa)
Trade Name	Pearlthane®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol Advanced Materials PearlthaneÂ® ECO D12T90 Thermoplastic Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Type : PearlthaneÂ® ECO D12T90 is a high performance bio-based thermoplastic polyurethane. With ca. 38% bio-based content.Main Application : Injection MouldingSpecial Features : Very good flexibility at low temperatures and very good abrasion resistance.

Physical Properties	Metric	English	Comments
Specific Gravity	1.15 g/cc	1.15 g/cc	ISO 2781

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	91	91	ISO 868
Tensile Strength	39.07 MPa	5667 psi	ISO 527-2/5A/500
Elongation at Break	470 %	470 %	ISO 527-2/5A/500
50% Modulus	0.00600 GPa	0.870 ksi	ISO 527-2/5A/500
100% Modulus	0.00900 GPa	1.31 ksi	ISO 527-2/5A/500
300% Modulus	0.0250 GPa	3.63 ksi	ISO 527-2/5A/500
Tear Strength	122 kN/m	697 pli	Die C; ISO 34-1B
Abrasion	35	35	mm<sup>3</sup> Loss; ISO 4649-A

Thermal Properties	Metric	English	Comments
Vicat Softening Point	108 Â°C	226 Â°F	ISO 306

Processing Properties	Metric	English
Feed Temperature	40.0 Â°C	104 Â°F
Nozzle Temperature	205 - 215 Â°C	401 - 419 Â°F
Zone 1	190 - 200 Â°C	374 - 392 Â°F
Zone 2	195 - 205 Â°C	383 - 401 Â°F
Zone 3	200 - 210 Â°C	392 - 410 Â°F
Zone 4	200 - 210 Â°C	392 - 410 Â°F
Dry Time	3.00 hour @Temperature 80.0 Â°C	3.00 hour @Temperature 176 Â°F

Descriptive Properties	Value	Comments
Biobased Content (%)	37	ASTM D-6866
Compression Zone Temperature	385Â°F
Metering Zone Temperature	390Â°F

Users viewing this material also viewed the following: