Polymer Property : Tensile Strength, Ultimate = 125000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	864 MPa @Thickness 12.7 mm, Temperature 20.0 Â°C	125000 psi @Thickness 0.500 in, Temperature 68.0 Â°F
Haynes HastelloyÂ® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	865 MPa @Thickness 3.20 mm, Temperature 25.0 Â°C	125000 psi @Thickness 0.126 in, Temperature 77.0 Â°F	As Welded; Weld/Weld Fracture
Haynes 282Â® Nickel Alloy Autogenously Welded Sheet Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Tensile Strength, Ultimate	860 MPa @Diameter 12.7 mm	125000 psi @Diameter 0.500 in	As Welded
Haynes 282Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Tensile Strength, Ultimate	860 MPa @Temperature 425 Â°C	125000 psi @Temperature 797 Â°F	Precipitation Hardened prior to test
Special Metals MONELÂ® Alloy K-500 A precipitation-hardenable nickel-copper alloy that combines the corrosion resistance of MONEL alloy 400 with greater strength and hardness. It also has low permeability and is nonmagnetic to under..
Tensile Strength, Ultimate	862 MPa @Thickness 127 - 152 mm	125000 psi @Thickness 5.00 - 6.00 in	Aquamet 22 HS
Crucible Steel Aquamet® 22 Stainless Steel AQUAMET 22 is a high-alloy stainless steel with superior corrosion resistance along with excellent toughness and high strength. It has higher strength than AQUAMET 17 in 3/4" to 1-1/4" dia., and it ..
Tensile Strength, Ultimate	865 MPa @Temperature 23.0 °C	125000 psi @Temperature 73.4 °F
ATI Allegheny Ludlum Stainless Steel Type 201L, 5% Cold Work (UNS S20103) Allegheny Ludlum Types 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201L provides advantages over the 18-8 grades in certain applications. Lower cost manganese ..
Tensile Strength, Ultimate	863 MPa @Thickness 12.7 mm	125000 psi @Thickness 0.500 in
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..