Polymer Property : Tensile Strength, Yield = 90000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	621 MPa @Temperature 23.9 °C	90000 psi @Temperature 75.0 °F	0° Direction, Dry; ASTM D638
Park Electrochemical Nelcote® E-720 Epoxy Prepreg, 581 Quartz Reinforced Nelcote® E-720 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-720 has a proven history in many demanding aerospac..
Tensile Strength, Yield	621 MPa @Temperature 21.1 °C	90000 psi @Temperature 70.0 °F	0° Direction, Wet; ASTM D638
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 3K PW Carbon Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Tensile Strength, Yield	>= 621 MPa @Strain 0.200 %, Thickness 0.127 - 0.254 mm	>= 90000 psi @Strain 0.200 %, Thickness 0.00500 - 0.0100 in	ASTM E-8
H.C. Starck Pure Molybdenum, Sheet Premium Grade PS-100-2 Description of Product: Rolled molybdenum sheet produced from pressed and sintered powder metallurgy sheet bar.Structure: Sheet will be supplied in a stress-relieved condition unless otherwise req..
Tensile Strength, Yield	>= 621 MPa @Strain 0.200 %, Thickness 0.254 - 0.508 mm	>= 90000 psi @Strain 0.200 %, Thickness 0.0100 - 0.0200 in	ASTM E-8
H.C. Starck Pure Molybdenum, Sheet Premium Grade PS-100-2 Description of Product: Rolled molybdenum sheet produced from pressed and sintered powder metallurgy sheet bar.Structure: Sheet will be supplied in a stress-relieved condition unless otherwise req..
Tensile Strength, Yield	>= 621 MPa @Strain 0.200 %, Thickness 0.127 - 0.254 mm	>= 90000 psi @Strain 0.200 %, Thickness 0.00500 - 0.0100 in	ASTM E-8
H.C. Starck 3202 Pure Molybdenum ASL, Arc-Cast, Low Carbon Sheet Arc-Cast Sheet 3202 Low CarbonDescription of Product: This specification covers rolled sheet of carbon-deoxidized molybdenum produced from sheet bar consolidated by the H.C. Starck consumable elect..
Tensile Strength, Yield	>= 621 MPa @Strain 0.200 %, Thickness 0.254 - 0.508 mm	>= 90000 psi @Strain 0.200 %, Thickness 0.0100 - 0.0200 in	ASTM E-8
H.C. Starck 3202 Pure Molybdenum ASL, Arc-Cast, Low Carbon Sheet Arc-Cast Sheet 3202 Low CarbonDescription of Product: This specification covers rolled sheet of carbon-deoxidized molybdenum produced from sheet bar consolidated by the H.C. Starck consumable elect..
Tensile Strength, Yield	621 MPa @Strain 0.200 %, Thickness <=44.5 mm	90000 psi @Strain 0.200 %, Thickness <=1.75 in	Tension
Crucible Steel Aquamet® 18 Stainless Steel AQUAMET 18 is an austenitic stainless steel with corrosion resistance comparable to that of Type 304. Its good strength and toughness make it an ideal shafting material for workboats. It provides a ..
Tensile Strength, Yield	621 MPa @Strain 0.200 %, Thickness 127 - 152 mm	90000 psi @Strain 0.200 %, Thickness 5.00 - 6.00 in	Tension; Aquamet 22 HS
Crucible Steel Aquamet® 22 Stainless Steel AQUAMET 22 is a high-alloy stainless steel with superior corrosion resistance along with excellent toughness and high strength. It has higher strength than AQUAMET 17 in 3/4" to 1-1/4" dia., and it ..
Tensile Strength, Yield	>= 621 MPa @Strain 0.500 %, Thickness 25.4 - 50.8 mm	>= 90000 psi @Strain 0.500 %, Thickness 1.00 - 2.00 in
Cadi 1 MOLD-MOR™ A very hard heat treatable copper alloy with moderate electrical conductivity. C18000 offers excellent value for the properties it offers. C18000 is a viable substitute for C17500 and C17510 for m..
Tensile Strength, Yield	>= 621 MPa @Strain 0.500 %, Thickness 25.4 - 50.8 mm	>= 90000 psi @Strain 0.500 %, Thickness 1.00 - 2.00 in
Cadi 10 MOLD-MOR™ A Copper Nickel Silicon Chromium Alloy with high thermal conductivity and moderate hardness.Information provided by Cadi Company.
Tensile Strength, Yield	>= 621 MPa @Strain 0.500 %, Thickness 25.4 - 50.8 mm	>= 90000 psi @Strain 0.500 %, Thickness 1.00 - 2.00 in
Cadi 2 MOLD-MOR™ A very hard heat treatable beryllium-copper alloy with moderate electrical conductivity. C17510 can be utilized when a combination of very good mechanical strength along with moderate electrical an..
Tensile Strength, Yield	>= 621 MPa @Strain 0.500 %, Thickness 25.4 - 50.8 mm	>= 90000 psi @Strain 0.500 %, Thickness 1.00 - 2.00 in
Cadi 20 MOLD-MOR™ A Beryllium Copper Alloy with high thermal conductivity and moderate hardness.Information provided by Cadi Company.
Tensile Strength, Yield	>= 621 MPa @Strain 0.500 %, Thickness 25.4 - 50.8 mm	>= 90000 psi @Strain 0.500 %, Thickness 1.00 - 2.00 in
Cadi C17500 Copper Alloy Information provided by Cadi Company.