Chosun Refractories CSN-601N Plate Brick
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories CSN-601N Plate Brick.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 3.10 - 3.20 g/cc | 0.112 - 0.116 lb/in³ | |
| Porosity | 5.0 - 8.0 % | 5.0 - 8.0 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | <= 0.00981 GPa @Temperature 1400 °C |
<= 1.42 ksi @Temperature 2550 °F |
|
| Compressive Strength | <= 147 MPa | <= 21300 psi | Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.00 - 10.0 µm/m-°C @Temperature 1000 °C |
4.44 - 5.56 µin/in-°F @Temperature 1830 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 72 - 76 % | 72 - 76 % | |
| Carbon, C | 10 - 13 % | 10 - 13 % | |
| ZrO2 | 4.0 - 6.0 % | 4.0 - 6.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Remarks | Spalling resistance, Excellent corrosion resistance, Oxidation resistance |
Users viewing this material also viewed the following:
- Techmer ES Electrablend® TPX-HTN-01045 A 40% Carbon Filled
- Teknor Apex Chemlon® 233 GH Nylon, 6, 30% Short Glass Fiber Reinforced
- Chesterton 415 Concrete Sealer
- Dow Corning TM-1950 EMULSION
- ExxonMobil LDPE LD 157CW Wire & Cable Low Density Polyethylene Resin
- ExxonMobil Mobil Vaculine 548
- Fainplast Compounds HG 81 Flexible PVC, Sheathing for High Temperatures
- ExxonMobil Exceed™ 3518 PA Premium Cast Film Resin
- Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound, Annealed 2 hours at 200°C (discontinued **)&l
- Johnson Matthey JM Tenacity 2 Brazing Flux Powder
Copyright © lookpolymers.com All Rights Reserved