Teknor Apex Chemlon® 233 GH Nylon, 6, 30% Short Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer Teknor Apex Company
Trade Name Chemlon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teknor Apex Chemlon® 233 GH Nylon, 6, 30% Short Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Good Dimensional Stability; Good Impact Resistance; Good Processability; Good Toughness; Heat Stabilized; High Strength; Lubricated Processing Method: Injection Molding Forms: Pellets Additive: Heat Stabilizer Automotive Specifications: GM GMP.PA6.009Information Provided by Teknor Apex
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength 169 MPa
24500 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
Elongation at Yield 3.0 %
3.0 %
ASTM D638
Flexural Strength 241 MPa
35000 psi
ASTM D790
Flexural Modulus 8.27 GPa
1200 ksi
ASTM D790
Izod Impact, Notched 1.44 J/cm

@Temperature 22.8 °C
 2.70 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear 52.2 µm/m-°C
29.0 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 212 °C
413 °F
Unannealed; ASTM D648
UL RTI, Electrical 105 °C

@Thickness 0.810 mm
 221 °F

@Thickness 0.0319 in
 UL 746
105 °C

@Thickness 1.50 mm
 221 °F

@Thickness 0.0590 in
 UL 746
105 °C

@Thickness 3.00 mm
 221 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 105 °C

@Thickness 0.810 mm
 221 °F

@Thickness 0.0319 in
 UL 746
105 °C

@Thickness 1.50 mm
 221 °F

@Thickness 0.0590 in
 UL 746
105 °C

@Thickness 3.00 mm
 221 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 105 °C

@Thickness 0.810 mm
 221 °F

@Thickness 0.0319 in
 UL 746
105 °C

@Thickness 1.50 mm
 221 °F

@Thickness 0.0590 in
 UL 746
105 °C

@Thickness 3.00 mm
 221 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 HB

@Thickness 0.810 mm
 HB

@Thickness 0.0319 in
Oxygen Index 22 %
22 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Strength 11.0 kV/mm

@Thickness 3.00 mm
 280 kV/in

@Thickness 0.118 in
 ASTM D149
Comparative Tracking Index 500 V
500 V
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 218 - 235 °C
425 - 455 °F
Middle Barrel Temperature 252 - 263 °C
485 - 505 °F
Front Barrel Temperature 252 - 268 °C
485 - 515 °F
Nozzle Temperature 252 - 268 °C
485 - 515 °F
Melt Temperature 216 °C
420 °F
Mold Temperature 60.0 - 93.3 °C
140 - 200 °F
Drying Temperature 79.4 °C
175 °F
Injection Pressure 34.5 - 138 MPa
5000 - 20000 psi
Screw Speed 60 - 120 rpm
60 - 120 rpm
Descriptive Properties Value Comments
Appearance Black
Suggested Moisture, max 0.2
Suggested Regrind, max 25