- Chase Plastics CP Pryme® NN113L (Dry) Nylon 66, 13% Glass Fiber Reinforced, Lubricated
Chase Plastics CP Pryme® NN113L (Dry) Nylon 66, 13% Glass Fiber Reinforced, Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® NN113L (Dry) Nylon 66, 13% Glass Fiber Reinforced, Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Good chemical resistanceGrease resistantLubricatedOil resistantHigh rigiditySolvent resistantHigh tensile strengthForm: PelletsInformation provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Filler Content | 13 % | 13 % | |
| Water Absorption | 1.0 % | 1.0 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 5.52 GPa | 800 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 734B (RL) Synthetic Oil
- Solvay TECHNYLSTARâ„¢ S 218 V35 PA6, 35% glass filled, DRY
- Shakespeare WP-104 diameter 0.4 mm Weft Polyester Monofilament
- SABIC Innovative Plastics LNP THERMOCOMP UF006H PPA (Asia Pacific)
- Teknor Apex Sinpolene MBW1444 Polypropylene
- A. Schulman COMTUF® 464 Glass Reinforced Impact Modified PBT Alloy
- ExxonMobil Mobil Permazone Coolant/Antifreeze
- ChevronTexaco Rykon® 5W-20 Premium Oil MV
- Arlon 19576R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved