CeramTec 965 Toughened Alumina (Al2O3-ZrO2)
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | CeramTec North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CeramTec 965 Toughened Alumina (Al2O3-ZrO2).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hasselman Thermal Shock value is 270 K.Data provided by CeramTec North America.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.20 g/cc | 0.152 lb/in³ | |
| Water Absorption | 0.00 % | 0.00 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Vickers Microhardness | 1450 | 1450 | HV 0.5 |
| Tensile Strength, Ultimate | 448 MPa | 65000 psi | ACMA Test #4 |
| Modulus of Elasticity | 344 GPa | 49900 ksi | Ultrasonic |
| Flexural Strength | 550 MPa | 79800 psi | 20 x 40 mm |
| Compressive Strength | 3586 MPa | 520100 psi | ASTM C773-88 |
| Poissons Ratio | 0.26 | 0.26 | ASTM C-1 259-94 |
| Fracture Toughness | 7.20 MPa-m½ | 6.55 ksi-in½ | |
| Shear Modulus | 139 GPa | 20200 ksi | Ultrasonic |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.00 µm/m-°C @Temperature 25.0 - 1001 °C |
4.44 µin/in-°F @Temperature 77.0 - 1834 °F |
|
| Specific Heat Capacity | 0.700 J/g-°C | 0.167 BTU/lb-°F | |
| Thermal Conductivity | 21.0 W/m-K | 146 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 1400 °C | 2550 °F |