- Carpenter Pyrowear® 675 Stainless Steel, Tempered 510°C, Transverse Properties
Carpenter Pyrowear® 675 Stainless Steel, Tempered 510°C, Transverse Properties
| Category | Metal , Ferrous Metal , Stainless Steel |
| Manufacturer | Carpenter Technology Corporation (Cartech) |
| Trade Name | Pyrowear® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Carpenter Pyrowear® 675 Stainless Steel, Tempered 510°C, Transverse Properties.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Carpenter Technology Corporation.This is a carburizing, corrosion resistant steel designed to provide a case hardness in excess of HRC 60 combined with a tough, ductile core. The corrosion resistance of carburized Pyrowear® 675 stainless is similar to that of Type 440C stainless, while the core toughness is similar to that of AISI 9310. In addition, the alloy provides excellent hot hardness capability. This alloy has been used in bearing and gear type applications.Pyrowear® is a registered trademark of Carpenter Technology Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.756 g/cc | 0.2802 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 379 | 379 | Estimated from Rockwell C for 3000 kg load, 10 mm ball Brinell measurement. |
| Hardness, Knoop | 414 | 414 | Estimated from Rockwell C |
| Hardness, Rockwell C | 41 | 41 | |
| Hardness, Vickers | 396 | 396 | Estimated from Rockwell C |
| Tensile Strength, Ultimate | 1276 MPa | 185100 psi | |
| Tensile Strength, Yield | 1062 MPa @Strain 0.200 % |
154000 psi @Strain 0.200 % |
|
| Elongation at Break | 18.5 % | 18.5 % | In 4D |
| Reduction of Area | 70 % | 70 % | |
| Modulus of Elasticity | 204 GPa | 29600 ksi | |
| Fracture Toughness | 86.0 MPa-m½ | 78.3 ksi-in½ | K(Q) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.01 µm/m-°C @Temperature 25.0 - 93.0 °C |
5.561 µin/in-°F @Temperature 77.0 - 199 °F |
|
| 10.62 µm/m-°C @Temperature 25.0 - 260 °C |
5.900 µin/in-°F @Temperature 77.0 - 500 °F |
||
| 11.56 µm/m-°C @Temperature 25.0 - 538 °C |
6.422 µin/in-°F @Temperature 77.0 - 1000 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.070 % | 0.070 % | |
| Chromium, Cr | 13 % | 13 % | |
| Cobalt, Co | 5.4 % | 5.4 % | |
| Iron, Fe | 76 % | 76 % | as remainder |
| Manganese, Mn | 0.65 % | 0.65 % | |
| Molybdenum, Mo | 1.8 % | 1.8 % | |
| Nickel, Ni | 2.6 % | 2.6 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Vanadium, V | 0.60 % | 0.60 % |