Carmel Olefins CAPILENE® SE 50 E Polypropylene Impact Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer Carmel Olefins
Trade Name CAPILENE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carmel Olefins CAPILENE® SE 50 E Polypropylene Impact Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: CAPILENE® SE 50 E is a low melt flow rate impact copolymer intended for sheet extrusion. It exhibits excellent impact strength even at low temperatures, combined with good processability, improved melt strength and good melt stability.Applications: CAPILENE® SE 50 E is suitable for extrusion applications like thin sheets, corrugated boards and profiles. It is also suitable for injection molding of technical components and for blow molding of hollow containers.Information provided by Carmel Olefins.
Physical Properties Metric English Comments
Melt Flow 1.3 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.3 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 24.0 MPa
3480 psi
50 mm/min; ASTM D638
Elongation at Yield 12 %
12 %
50 mm/min; ASTM D638
Flexural Modulus 1.15 GPa
167 ksi
ASTM D790
Izod Impact, Notched 0.600 J/cm

@Temperature -20.0 °C
1.12 ft-lb/in

@Temperature -4.00 °F
ASTM D256
5.50 J/cm

@Temperature 23.0 °C
10.3 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
ASTM D648
Vicat Softening Point 150 °C

@Load 1.02 kg
302 °F

@Load 2.25 lb
ASTM D1525