BASF Capron® 8260 HS BK-102 40% Mineral-Filled Nylon 6 (Conditioned)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 8260 HS BK-102 40% Mineral-Filled Nylon 6 (Conditioned)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced nylon 6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low warp and resistance to sink-mark formation. It maintains its inherent chemical resistance to greases, oils and hydrocarbons.Capron 8260 HS BK-102 is generally recommended for applications such as marine hardware, brackets, fittings, bobbins, office furniture, appliance components, and power tool housings.Data provided by Allied Signal.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
(Dry)
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM Data MD (Dry)
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO Data (Dry)
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 55.0 MPa
7980 psi
ASTM data at 5 mm/min.
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; Same value from ASTM and ISO test.
Elongation at Break 25 %
25 %
ASTM, 5 mm/minl
25 %
25 %
Nominal
Elongation at Yield 13 %
13 %
ISO Value at 50 mm/min.
15 %
15 %
ASTM Value at 50 mm/min.
Tensile Modulus 3.80 GPa
551 ksi
same value from ASTM and ISO test.
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
(Dry)
Processing Properties Metric English Comments
Processing Temperature 275 °C
527 °F
See Materials Notes
Mold Temperature 95.0 °C
203 °F
See Materials Notes