- Oxford Polymers PC GR912-V0 UL Listed Polycarbonate
Oxford Polymers PC GR912-V0 UL Listed Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers PC GR912-V0 UL Listed Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UL Listed PolycarbonateInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Modulus | 2.24 GPa | 325 ksi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm @Temperature 23.0 °C |
10.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8512SU (UF) Synthetic Oil
- SABIC Innovative Plastics Lexan® OQ2320 PC (Asia Pacific)
- Phillips 66 COPYLENE® CR020N Polypropylene Random Copolymer
- SABIC Innovative Plastics Lexan® 953 PC
- Haynes 556® alloy, bar after 16000 hours at 537°C
- Universal Wire Works BAg-1A (AMS 4770) Silver Brazing Filler Metal
- Wellman Wellamid® MRGF25/15 42H-GY1 40% Mineral/Glass Fiber Reinforced Nylon 6
- Total PS CPDS FT875 Flame Retardant Polystyrene
- Zircar Zirconia ALK-15 Alumina Knit Textile Insulation
- Asahi Kasei Thermofil P-40CC-1100 40% Calcium Carbonate Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved